エネルギー分散X線分光法により明らかにされた疲労損傷RC梁における塩化物濃度分布【JST・京大機械翻訳】

Chloride concentration distributions in fatigue damaged RC beams revealed by energy-dispersive X-ray spectroscopy

著者 (5件)： Wu Jieqiong (School of Transportation Science and Engineering, Beihang University, Beijing 100191, China) ,  Diao Bo (School of Transportation Science and Engineering, Beihang University, Beijing 100191, China) ,  Cao Yuan (Department of Civil & Mineral Engineering, University of Toronto, Toronto, ON M5S 1A4, Canada) ,  Zhong Jing (School of Civil Engineering, Harbin Institute of Technology, Harbin 150090, China) ,  Shi Xianming (Laboratory of Corrosion Science & Electrochemical Engineering, Department of Civil and Environmental Engineering, Washington State University, Pullman, WA 99164-2910, USA)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 234  ページ： Null  発行年： 2020年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,疲労損傷RC梁の鋼-コンクリート界面における塩化物濃度をエネルギー分散X線分光法により調べた。梁試料は3.5wt%NaCl溶液湿式乾燥サイクルに続く疲れ荷重を受けた。一つの梁における二つの棒に対して,疲労破壊鋼は,純粋な曲げ部分において,厳しい腐食(30%~40%の腐食面積)および高い塩化物濃度(0.5wt%~0.9wt%)を示した。荷重レベル(極限静的強度に対する最大疲れ荷重の比)が0.45に達したとき,または,疲れ荷重の1.2百万サイクル後に,疲れ損傷は,圧縮コンクリートの塩化物濃度に影響を及ぼした。0.4から0.45への荷重レベルの増加は,引張コンクリートの塩化物濃度を少なくとも30%増加させ,残留疲れ寿命を6.24倍減少させたが,初期疲れ荷重サイクルはそれらのいずれにもほとんど影響しなかった。塩化物濃度の結果は,残留疲れ寿命試験の結果と一致した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *疲れ損傷 ,  界面 ,  *エネルギー分散X線分光分析 ,  コンクリート ,  *梁 ,  寿命試験 ,  腐食 ,  *塩化物 ,  疲れ破壊 ,  *濃度分布 ,  鋼 ,  疲れ寿命 ,  疲れ荷重 ,  引張 ,  塩化ナトリウム

著者キーワード (5件)： 鉄筋腐食 ,  疲労損傷 ,  エネルギー分散型X線分光法(EDS) ,  塩化物濃度 ,  RC梁

分類 (1件)： コンクリート構造  (RA04030A)

タイトルに関連する用語 (5件)： エネルギー分散X線分光法 ,  疲労損傷 ,  RC梁 ,  塩化物 ,  濃度分布