種々の負荷での乾燥滑り条件下でのレーザテクスチャードタングステンドープダイヤモンド状炭素被覆のトライボロジー特性の実験的研究【JST・京大機械翻訳】

Experimental investigation of tribological properties of laser textured tungsten doped diamond like carbon coating under dry sliding conditions at various loads

著者 (20件)： Arslan A (Department of Mechanical Engineering, COMSATS University Islamabad, Sahiwal Campus, 57000, Pakistan) ,  Arslan A (Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Masjuki H H (Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Masjuki H H (Department of Mechanical Engineering, Faculty of Engineering, IIUM, 50728, Kuala Lumpur, Malaysia) ,  Quazi M M (Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Quazi M M (Faculty of Mechanical and Manufacturing Engineering, Universiti Malaysia Pahang, 26600 Pekan, Pahang, Malaysia) ,  Kalam M A (Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Varman M (Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Jamshaid M (Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Jamshaid M (Department of Mechanical Engineering, Bahauddin Zakariya University, Multan 60000, Pakistan) ,  Rahman S M Ashrafur (Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Rahman S M Ashrafur (Queensland University of Technology, Brisbane, QLD, Australia) ,  Imran M (Mechanical Engineering & Design, School of Engineering and Applied Science, Aston University, Aston Triangle, Birmingham B4 7ET, United Kingdom) ,  Zulfattah Z M (Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Zulfattah Z M (Center for Advanced Research on Energy (CARe), Fakulti Kejuruteraan Mekanikal, Universiti Teknikal Malaysia Melaka, 75450, Ayer Keroh, Melaka, Malaysia) ,  Anwar M T (Department of Mechanical Engineering, COMSATS University Islamabad, Sahiwal Campus, 57000, Pakistan) ,  Gohar G A (Department of Mechanical Engineering, COMSATS University Islamabad, Sahiwal Campus, 57000, Pakistan) ,  Mandalan S M (Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia) ,  Mandalan S M (Department of Mechanical Engineering, Faculty of Engineering, Bayero University, Kano, 3011, Nigeria) ,  Harith M H (Department of Mechanical Engineering, University of Malaya, 50603 Kuala Lumpur, Malaysia)
資料名： Materials Research Express  (Materials Research Express)
巻： 6  号： 10  ページ： 106444 (9pp)  発行年： 2019年 
JST資料番号： W5570A  ISSN： 2053-1591  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： レーザマイクロテクスチャリング技術は,自動車や切削工具などの種々の機械的界面での摩擦と摩耗の低減における可能性を示し,自動車部品はダイヤモンド状炭素(DLC)被覆で被覆され,その性能を向上させる。自動車接点の厳しい条件と性能向上の要求により,DLC被覆の性能の向上が必要である。本研究では,レーザミクロ組織化をタングステン添加DLC被覆と組み合わせた。タングステンをドープしたDLC被覆におけるレーザミクロ組織化の利点を解析した。トライボロジー試験を種々の荷重条件で往復試験装置で行った。結果は,レーザ組織化タングステンをドープしたDLC被覆が,15N,25Nおよび35Nの荷重で,非組織化タングステンをドープしたDLC被覆と比較して,より低い摩擦係数を示すことを示した。35N負荷での非組織化被覆の場合に,より高い黒鉛化が観察された。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面 ,  自動車 ,  摩擦係数 ,  試験装置 ,  *トライボロジー ,  摩耗 ,  *レーザ ,  切削工具 ,  *被覆 ,  黒鉛化 ,  *ドーピング ,  *タングステン
準シソーラス用語： DLC被覆 ,  自動車部品 ,  *トライボロジー特性 , 【Automatic Indexing@JST】