高性能ナノろ過膜のためのナノダイヤモンド媒介界面重合【JST・京大機械翻訳】

Nanodiamond mediated interfacial polymerization for high performance nanofiltration membrane

著者 (19件)： Qin Detao (Institute for Integrated Cell-Material Sciences (iCeMS), Kyoto University, 606-8501, Kyoto, Japan) ,  Qin Detao (Department of Molecular Engineering, Graduate School of Engineering, Kyoto University, Nishikyo-Ku, Kyoto, 615-8510, Japan) ,  Huang Guoji (Institute for Integrated Cell-Material Sciences (iCeMS), Kyoto University, 606-8501, Kyoto, Japan) ,  Huang Guoji (Department of Molecular Engineering, Graduate School of Engineering, Kyoto University, Nishikyo-Ku, Kyoto, 615-8510, Japan) ,  Terada Daiki (Department of Molecular Engineering, Graduate School of Engineering, Kyoto University, Nishikyo-Ku, Kyoto, 615-8510, Japan) ,  Jiang Handong (Institute for Integrated Cell-Material Sciences (iCeMS), Kyoto University, 606-8501, Kyoto, Japan) ,  Jiang Handong (Department of Molecular Engineering, Graduate School of Engineering, Kyoto University, Nishikyo-Ku, Kyoto, 615-8510, Japan) ,  Ito Masateru M. (Institute for Integrated Cell-Material Sciences (iCeMS), Kyoto University, 606-8501, Kyoto, Japan) ,  Ito Masateru M. (Department of Molecular Engineering, Graduate School of Engineering, Kyoto University, Nishikyo-Ku, Kyoto, 615-8510, Japan) ,  H. Gibbons Andrew (Institute for Integrated Cell-Material Sciences (iCeMS), Kyoto University, 606-8501, Kyoto, Japan) ,  H. Gibbons Andrew (Department of Molecular Engineering, Graduate School of Engineering, Kyoto University, Nishikyo-Ku, Kyoto, 615-8510, Japan) ,  Igarashi Ryuji (Institute for Quantum Life Science, National Institute for Quantum and Radiological Science and Technology, 4-9-1, Anagawa, Inage-Ku, Chiba, 263-8555, Japan) ,  Yamaguchi Daisuke (Institute for Integrated Cell-Material Sciences (iCeMS), Kyoto University, 606-8501, Kyoto, Japan) ,  Yamaguchi Daisuke (Department of Molecular Engineering, Graduate School of Engineering, Kyoto University, Nishikyo-Ku, Kyoto, 615-8510, Japan) ,  Shirakawa Masahiro (Department of Molecular Engineering, Graduate School of Engineering, Kyoto University, Nishikyo-Ku, Kyoto, 615-8510, Japan) ,  Sivaniah Easan (Institute for Integrated Cell-Material Sciences (iCeMS), Kyoto University, 606-8501, Kyoto, Japan) ,  Sivaniah Easan (Department of Molecular Engineering, Graduate School of Engineering, Kyoto University, Nishikyo-Ku, Kyoto, 615-8510, Japan) ,  Ghalei Behnam (Institute for Integrated Cell-Material Sciences (iCeMS), Kyoto University, 606-8501, Kyoto, Japan) ,  Ghalei Behnam (Department of Molecular Engineering, Graduate School of Engineering, Kyoto University, Nishikyo-Ku, Kyoto, 615-8510, Japan)
資料名： Journal of Membrane Science  (Journal of Membrane Science)
巻： 603  ページ： Null  発行年： 2020年 
JST資料番号： E0669A  ISSN： 0376-7388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： ナノろ過(NF)膜合成のための界面重合(IP)システムにナノ材料を導入することにより,顕著な性能向上が得られ,集中的な注意が得られるようになった。しかし,ナノ材料誘起性能増強の基礎となる機構は,重合界面におけるナノ粒子の分散と構造に関する研究の欠如により,依然として不明である。例としてナノダイヤモンド(ND)を用いて,本研究はナノ粒子が反応界面で優先的に凝集し,ND粒子の構造が膜構造と性能に直接影響することを実証した。ナノ鋳型としてこれらのNDクラスタを使用しながら,凝集範囲を積極的に制御することにより,NF膜の特徴形態をナノスケールでノジュールからリッジに変換した。このような変換は有効な膜面積の顕著な増大をもたらし,水透過率を70%増加させる。少量のナノダイヤモンド添加(<0.1wt%)により,NF膜は,Na_2SO_4の約98%の除去率で,150Lm-2h(-1)MPa(-1)の高い水透過率を達成することができた。さらに,ナノダイヤモンドの導入は,水接触角を50°から35°に減少させると,ナノ濾過膜をより親水性にする。現代のナノフィラー研究との比較は,著者らのナノダイヤモンド戦略が最良の性能向上のいくつかをもたらすことを示した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *界面 ,  凝集 ,  *重合 ,  親水性 ,  *界面重合 ,  団塊 ,  クラスタ ,  膜構造 ,  透過率 ,  ナノ粒子 ,  ナノ材料
準シソーラス用語： ナノスケール ,  *ナノダイヤモンド ,  ナノフィラー ,  *ナノ濾過膜 , 【Automatic Indexing@JST】

著者キーワード (5件)： ナノろ過膜 ,  水処理 ,  界面重合 ,  ナノダイヤモンド ,  ナノ粒子凝集制御