二段時効処理によるAl-Cu-Mg-Fe-Ni合金の性質とミクロ組織に関する研究【JST・京大機械翻訳】

Study on properties and microstructure of an Al-Cu-Mg-Fe-Ni alloy with two-stage aging treatment

著者 (5件)： Su Ruiming (Shenyang University of Technology, School of Materials Science and Engineering, Shenyang 110870, People’s Republic of China) ,  Xiao Jian (Shenyang University of Technology, School of Materials Science and Engineering, Shenyang 110870, People’s Republic of China) ,  Jia Yongxin (Shenyang University of Technology, School of Materials Science and Engineering, Shenyang 110870, People’s Republic of China) ,  Wang Kaining (Shenyang University of Technology, School of Materials Science and Engineering, Shenyang 110870, People’s Republic of China) ,  Qu Yingdong (Shenyang University of Technology, School of Materials Science and Engineering, Shenyang 110870, People’s Republic of China)
資料名： Materials Research Express  (Materials Research Express)
巻： 6  号： 12  ページ： 126561 (9pp)  発行年： 2019年 
JST資料番号： W5570A  ISSN： 2053-1591  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Al-Cu-Mg-Fe-Ni合金は良好な高温特性を有し,二段階時効熱処理により改善できる。Taguchi法により実験と解析を行い,最良の実験条件を決定した。現在,最適化されたターゲットとして合金の硬度と引張強さがある。最適化条件として,第一段階時効温度,第一段階時効時間,第二段階時効温度および第二段階時効時間の4つの影響因子を検討した。合金の硬度と引張特性を試験した。結果は,最良の二段階時効熱処理プロセスが180°Cの8時間の第一段階時効条件であり,240°Cの第二段階時効条件が6時間であることを示した。高温での合金の引張強さは,30MPa上下に改善された。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 熱処理 ,  *合金 ,  最適化 ,  硬度 ,  *時効 ,  高温 ,  引張強さ
準シソーラス用語： 引張特性 ,  影響因子 ,  高温特性 ,  鉄-ニッケル , 【Automatic Indexing@JST】

分類 (3件)： 熱処理技術  (WC03020T) ,  機械的性質  (WB02030U) ,  組織的硬化現象  (WB01020C)

タイトルに関連する用語 (8件)： 時効処理 ,  Al ,  Cu ,  Mg ,  Fe-Ni合金 ,  性質 ,  ミクロ組織 ,  研究