800°Cでの混合酸化浸炭雰囲気に曝されたNi-Cr-Al合金の腐食挙動【JST・京大機械翻訳】

The corrosion behavior of Ni-Cr-Al alloys exposed to mixed oxidizing-carburizing atmospheres at 800 °C

著者 (8件)： Guo X.H. (Institute of Metal Research, Chinese Academy of Science, Shenyang, China) ,  Guo X.H. (School of Materials & Engineering, University of Science & Technology of China, Hefei, China) ,  Shen J. (Institute of Metal Research, Chinese Academy of Science, Shenyang, China) ,  Shen J. (School of Energy & Power Engineering, Changsha University of Science & Technology, Changsha, China) ,  Liu S. (Industrial Training Centre, Shenzhen Polytechnic, Shenzhen, China) ,  Chen J. (School of Energy & Power Engineering, Changsha University of Science & Technology, Changsha, China) ,  Niu Y. (Institute of Metal Research, Chinese Academy of Science, Shenyang, China) ,  Niu Y. (School of Energy & Power Engineering, Changsha University of Science & Technology, Changsha, China)
資料名： Corrosion Science  (Corrosion Science)
巻： 176  ページ： Null  発行年： 2020年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： Ni-10/15Cr-7AlとNi-5Cr-10Al(at.%)を800°Cで3つのC/O混合ガスに暴露し,2つ(Gase1,2)はクロムとアルミニウムの両方を酸化し,一方3番目のガス(Gas3)はアルミニウムのみを酸化できた。Ni-5Cr-10Alは常にアルミナスケールを形成した。Ni-10/15Cr-7Alとガス1および2との反応は外部クロミアプラス内部アルミナを形成し,一方ガス3は外部アルミナ+内部炭化クロムを生成した。ガス3におけるNi-10/15Cr-7Al上の外部アルミナ成長は,ガス1と2に関して内部から外部への酸化のための臨界アルミニウム含有量の減少に起因する。酸化マップを用いて,ガス1と2の結果を説明した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  混合気体 ,  *酸化 ,  *アルミニウム ,  クロム ,  アルミナ ,  臨界
準シソーラス用語： 炭化クロム ,  *腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： 合金 ,  SEM ,  高温腐食 ,  浸炭 ,  内部酸化