異なる加熱モードで焼結した炭化ケイ素強化W-Ni-Cu基重合金の研究【JST・京大機械翻訳】

A study of silicon carbide reinforced W-Ni-Cu based heavy alloys sintered with different heating modes

著者 (5件)： Annamalai A Raja (Centre for Innovative Manufacturing Research, Vellore Institute of Technology, Vellore -632 014, Tamil Nadu, India) ,  Chaurasia Jitender Kumar (Department of Manufacturing Engineering, School of Mechanical Engineering, VIT Vellore -632 014, Tamil Nadu, India) ,  Srikanth Muthe (Department of Manufacturing Engineering, School of Mechanical Engineering, VIT Vellore -632 014, Tamil Nadu, India) ,  Agrawal Dinesh K (Materials Research Institute, The Pennsylvania State University, University Park, PA 16802, United States of America) ,  Jen Chun-Ping (Department of Mechanical Engineering, National Chung Cheng University, Chia-Yi, Taiwan)
資料名： Materials Research Express  (Materials Research Express)
巻： 7  号： 12  ページ： 126503 (9pp)  発行年： 2020年 
JST資料番号： W5570A  ISSN： 2053-1591  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,W-Ni-Cu系重合金への炭化ケイ素(SiC)添加の影響を調べた。SiCの百分率を変えたW-Ni-Cu粉末を混合し,通常および放電プラズマ焼結(SPS)法を用いて焼結した。焼結試料を,密度,微細構造,および機械的性質を決定するために特性評価した。合金(W-7Ni-3Cu-0.5SiC)は,通常の焼結と放電プラズマ焼結で,それぞれ,従来の焼結と放電プラズマ焼結の831MPaと,従来の焼結と放電プラズマ焼結で,それぞれ,高い極限引張強度430MPaを示した。引張試験後,破面は脆性W/W粒界とマトリックス中の破壊の延性モードから成る混合モード破壊を示した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 延性 ,  機械的性質 ,  結晶粒界 ,  *合金 ,  *焼結 ,  微細構造 ,  引張試験 ,  粉体 ,  脆性 ,  *炭化ケイ素 ,  破面 ,  引張強さ ,  混合モード ,  放電プラズマ焼結
準シソーラス用語： *重合金 , 【Automatic Indexing@JST】

分類 (2件)： 圧粉,焼結  (WC02030X) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (7件)： 焼結 ,  炭化ケイ素 ,  強化 ,  Ni ,  Cu ,  重合金 ,  研究