単一成分ポリウレタン多孔質弾性混合物の硬化性能【JST・京大機械翻訳】

Curing Performance of Monocomponent Polyurethane Porous Elastic Mixture

著者 (7件)： Zhong Ke (Research Institute of Highway Ministry of Transport, Beijing, 100088, China) ,  Zhang Meng (Research Institute of Highway Ministry of Transport, Beijing, 100088, China) ,  Zhang Meng (Key Laboratory of Transport Industry of Road Structure and Material, Beijing, 100088, China.) ,  Sun Mingzhi (Research Institute of Highway Ministry of Transport, Beijing, 100088, China) ,  Sun Mingzhi (Key Laboratory of Transport Industry of Road Structure and Material, Beijing, 100088, China.) ,  Wang Xue (Chongqing Jiaotong University, Chongqing, China) ,  Sun Shengkai (Chongqing Jiaotong University, Chongqing, China)
資料名： IOP Conference Series: Earth and Environmental Science  (IOP Conference Series: Earth and Environmental Science)
巻： 565  号： 1  ページ： 012065 (6pp)  発行年： 2020年 
JST資料番号： W5558A  ISSN： 1755-1307  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ポリウレタン(PU)は一種のクリーン材料であり,舗装工学における多孔質弾性混合物の結合材として利用できる。本論文では,単成分ポリウレタン多孔質弾性混合物の硬化性能を調べた。単成分ポリウレタンおよびポリウレタン多孔質弾性混合物(PPEM)の硬化性能を分析するために,Fourier変換赤外スペクトル(FTIR)およびMarshall試験を行った。結果は,PPEM-IとPPEM-IIが4日間の硬化後にほぼ完全に硬化することを示した。Marshall安定性に関して,PPEM-IとPPEM-IIは4日間の硬化後にほぼ完全に硬化した。そして,PPEM-IのMarshall安定性は,同じ室硬化条件の下で,PPEM-IIのものより高い。一方,水-PPEM比が2%,PPEM-IとPPEM-IIのMarshall安定性が4日の室温硬化条件試料に近いとき,水散水法は硬化速度を改善するために採用することができる。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： Fourier変換 ,  赤外スペクトル ,  *ポリウレタン ,  結合材料 ,  散水 ,  FTIR分光法
準シソーラス用語： *多孔質弾性 , 【Automatic Indexing@JST】