マンガンへのリン比の調整によるQ235炭素鋼上の顕著な耐食性を有するMn-P皮膜の形成に関する研究【JST・京大機械翻訳】

Study on the formation of Mn-P coatings with significant corrosion resistance on Q235 carbon steels by adjusting the ratio of phosphorus to manganese

著者 (7件)： Guo Lihua (School of Chemical Engineering, Zhengzhou University, Zhengzhou, 450001, PR China) ,  Huang Qiang (School of Chemical Engineering, Zhengzhou University, Zhengzhou, 450001, PR China) ,  Zhang Cong (School of Chemical Engineering, Zhengzhou University, Zhengzhou, 450001, PR China) ,  Wang Jie (School of Chemical Engineering, Zhengzhou University, Zhengzhou, 450001, PR China) ,  Shen Guopeng (School of Chemical Engineering, Zhengzhou University, Zhengzhou, 450001, PR China) ,  Ban Chunlan (School of Chemical Engineering, Zhengzhou University, Zhengzhou, 450001, PR China) ,  Guo Linxuan (School of Chemical Engineering, Zhengzhou University, Zhengzhou, 450001, PR China)
資料名： Corrosion Science  (Corrosion Science)
巻： 178  ページ： Null  発行年： 2021年 
JST資料番号： B0135B  ISSN： 0010-938X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： リン-マンガン比を変えて調製したMn-P被覆はQ235炭素鋼の耐食性を著しく改善する。表面形態,コーティングの組成を,エネルギー分散分光(EDS),X線回折(XRD)およびX線光電子分光法(XPS)を備えた走査電子顕微鏡(SEM)により分析した。コーティングの耐食性を動電位分極(PDP),電気化学インピーダンス分光法(EIS)および塩水噴霧試験(SST)により評価した。実験は,Mn2+:PO_43-=1:7,塩噴霧が30時間以上に耐えることができ,明白な腐食がないとき,薄くて緻密なコーティングが得られることを証明した。最後に,成長機構を説明した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  走査電子顕微鏡 ,  電子顕微鏡観察 ,  *マンガン ,  *リン ,  *炭素鋼 ,  被覆 ,  *耐食性 ,  X線回折分析 ,  塩水噴霧試験 ,  噴霧 ,  *皮膜 ,  X線光電子分光法 ,  エネルギー散逸
準シソーラス用語： 表面形態 ,  動電位分極 ,  電気化学インピーダンス分光法 , 【Automatic Indexing@JST】

著者キーワード (5件)： Q235炭素鋼 ,  Mn-Pコーティング ,  耐食性 ,  リン-マンガン比 ,  成長機構