高圧下の模擬海水掘削流体におけるHVOF溶射WC-10Co4Cr被覆の腐食挙動【JST・京大機械翻訳】

Corrosion behavior of HVOF sprayed WC-10Co4Cr coatings in the simulated seawater drilling fluid under the high pressure

著者 (22件)： Zhou Yong-kuan (School of Engineering and Technology, China University of Geosciences (Beijing), Beijing 100083, China) ,  Liu Xiao-bin (School of Engineering and Technology, China University of Geosciences (Beijing), Beijing 100083, China) ,  Kang Jia-jie (School of Engineering and Technology, China University of Geosciences (Beijing), Beijing 100083, China) ,  Kang Jia-jie (Key Laboratory of Deep GeoDrilling Technology of Ministry of Natural Resources, Beijing 100083, China) ,  Kang Jia-jie (Zhengzhou Institute, China University of Geosciences (Beijing), Zhengzhou 451283, China) ,  Yue Wen (School of Engineering and Technology, China University of Geosciences (Beijing), Beijing 100083, China) ,  Yue Wen (Zhengzhou Institute, China University of Geosciences (Beijing), Zhengzhou 451283, China) ,  Qin Wen-bo (School of Engineering and Technology, China University of Geosciences (Beijing), Beijing 100083, China) ,  Ma Guo-zheng (National Key Lab for Remanufacturing, Academy of Armored Forces Engineering, Beijing 100072, China) ,  Fu Zhi-qiang (School of Engineering and Technology, China University of Geosciences (Beijing), Beijing 100083, China) ,  Fu Zhi-qiang (Zhengzhou Institute, China University of Geosciences (Beijing), Zhengzhou 451283, China) ,  Zhu Li-na (School of Engineering and Technology, China University of Geosciences (Beijing), Beijing 100083, China) ,  Zhu Li-na (Zhengzhou Institute, China University of Geosciences (Beijing), Zhengzhou 451283, China) ,  She Ding-shun (School of Engineering and Technology, China University of Geosciences (Beijing), Beijing 100083, China) ,  She Ding-shun (Zhengzhou Institute, China University of Geosciences (Beijing), Zhengzhou 451283, China) ,  Wang Hai-dou (School of Engineering and Technology, China University of Geosciences (Beijing), Beijing 100083, China) ,  Wang Hai-dou (National Key Lab for Remanufacturing, Academy of Armored Forces Engineering, Beijing 100072, China) ,  Liang Jian (School of Engineering and Technology, China University of Geosciences (Beijing), Beijing 100083, China) ,  Liang Jian (Institute of Exploration Techniques, Chinese Academy of Geological Sciences, Langfang 065000, China) ,  Weng Wei (Beijing Institute of Exploration Engineering, China Geological Survey, Beijing 100083, China) ,  Wang Cheng-biao (Zhengzhou Institute, China University of Geosciences (Beijing), Zhengzhou 451283, China) ,  Wang Cheng-biao (Zhengzhou Institute of Multipurpose Utilization of Mineral Resources, Chinese Academy of Geological Sciences, Zhengzhou 450006, China)
資料名： Engineering Failure Analysis  (Engineering Failure Analysis)
巻： 109  ページ： Null  発行年： 2020年 
JST資料番号： W0684A  ISSN： 1350-6307  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高速度酸素燃料(HVOF)技術により,35CrMo鋼(ANSI/ASTM 4135)基板上に,通常の(ミクロンサイズWC粒子)および二モード(ナノサイズおよびミクロンサイズWC粒子の混合物)構造を有する2種類のWC-10Co4Cr複合材料被覆を成功裏に調製した。エネルギー分散分光法(EDS),機械的試験機,微小硬さ試験機を装備した走査電子顕微鏡(SEM)を用いて,皮膜の特性を分析した。コーティングを,深海環境をシミュレートするために,高圧下で模擬海水掘削液に浸漬し,次に,電気化学インピーダンス分光法(EIS),動電位分極を行い,コーティングと基板の電気化学的性質を研究した。結果は,WC-10Co4Crコーティングが優れた耐食性を有し,高圧下で基板を効果的に保護できることを示した。さらに,従来のコーティング(CC)と比較して,二モードコーティング(BC)は,より高密度の微細構造,優れた機械的性質,より低い気孔率,およびより良い耐食性を有していた。高圧下の模擬海水掘削液中の被覆の腐食機構は以下の通りである。WC相とCoCrバインダ相との間の微小ガルバニ腐食が主要な腐食機構である。その上,高圧下の電解質はより浸透性があり,したがって,隙間腐食も存在する。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *被覆 ,  電子顕微鏡観察 ,  電池作用腐食 ,  深海 ,  *高圧 ,  機械的性質 ,  走査電子顕微鏡 ,  耐食性 ,  酸素 ,  隙間腐食 ,  電解質 ,  *掘削液 ,  粘結剤 ,  皮膜 ,  鋼 ,  腐食機構

著者キーワード (5件)： 高速酸素燃料 ,  WC-10Co4Cr ,  従来法 ,  バイモーダル ,  耐食性

分類 (2件)： 腐食  (WB03030B) ,  蒸気タービン  (PB01040R)

タイトルに関連する用語 (6件)： 高圧 ,  海水 ,  掘削流体 ,  HVOF溶射 ,  WC ,  腐食挙動