Layer-by-layer corrosion behavior of 316LN stainless steel with a gradient-nanostructured surface

著者 (6件)： Chen Xudong (Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Li Yusheng (Nano and Heterogeneous Materials Center, School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, China) ,  Zhu Yuntian (Nano and Heterogeneous Materials Center, School of Materials Science and Engineering, Nanjing University of Science and Technology, Nanjing 210094, China) ,  Zhu Yuntian (Department of Materials Science and Engineering, North Carolina State University, Raleigh, NC 27695, USA) ,  Chen Yuefeng (Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China) ,  Yang Bin (Collaborative Innovation Center of Steel Technology, University of Science and Technology Beijing, Beijing 100083, China)
資料名： Electrochemistry Communications  (Electrochemistry Communications)
巻： 110  ページ： Null  発行年： 2020年 
JST資料番号： W1133A  ISSN： 1388-2481  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 傾斜ナノ構造表面層を有する316LNステンレス鋼を回転加速ショットピーニング(RASP)により作製した。この勾配層の厚さは約210μmであった。層毎の電気化学実験により,最良の耐食性を有する傾斜鋼の層が表面から110μmの距離で見出されることを確認した。RASPにより生成されたナノ構造とピットは,その耐食性に対して2つの反対の効果を生じた:ナノ結晶とナノ双晶は,腐食に抵抗する厚いコンパクトな不動態皮膜の形成を容易にし,一方,ピットはそれを破壊する傾向がある。ピット上と滑らかにナノ構造化された領域上に形成された不動態膜は,それぞれ5.5nmと13.9nmの厚さであった。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *ナノ構造 ,  *ステンレス鋼 ,  ショットピーニング ,  耐食性 ,  不動態皮膜 ,  電気化学 ,  ナノ結晶 ,  *鋼 ,  表層
準シソーラス用語： ナノ双晶 ,  *腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： ステンレス鋼 ,  傾斜構造 ,  パッシブフィルム ,  耐食性

分類 (1件)： 電極過程  (CB07040U)

タイトルに関連する用語 (4件)： ナノ構造 ,  316LNステンレス鋼 ,  層 ,  腐食挙動