短いCF/GF強化PEEK複合材料フィラメントの調製とFDM-3D印刷のためのそれらの包括的な特性評価【JST・京大機械翻訳】

Preparation of short CF/GF reinforced PEEK composite filaments and their comprehensive properties evaluation for FDM-3D printing

著者 (19件)： Wang Peng (Centre for Advanced Jet Engineering Technologies (CaJET), School of Mechanical Engineering, Shandong University, Jinan, 250061, PR China) ,  Wang Peng (Key Laboratory of High-Efficiency and Clean Mechanical Manufacture at Shandong University, Ministry of Education, PR China) ,  Wang Peng (National Demonstration Center for Experimental Mechanical Engineering Education, Shandong University, PR China) ,  Zou Bin (Centre for Advanced Jet Engineering Technologies (CaJET), School of Mechanical Engineering, Shandong University, Jinan, 250061, PR China) ,  Zou Bin (Key Laboratory of High-Efficiency and Clean Mechanical Manufacture at Shandong University, Ministry of Education, PR China) ,  Zou Bin (National Demonstration Center for Experimental Mechanical Engineering Education, Shandong University, PR China) ,  Ding Shouling (Centre for Advanced Jet Engineering Technologies (CaJET), School of Mechanical Engineering, Shandong University, Jinan, 250061, PR China) ,  Ding Shouling (Key Laboratory of High-Efficiency and Clean Mechanical Manufacture at Shandong University, Ministry of Education, PR China) ,  Ding Shouling (National Demonstration Center for Experimental Mechanical Engineering Education, Shandong University, PR China) ,  Huang Chuanzhen (Centre for Advanced Jet Engineering Technologies (CaJET), School of Mechanical Engineering, Shandong University, Jinan, 250061, PR China) ,  Huang Chuanzhen (Key Laboratory of High-Efficiency and Clean Mechanical Manufacture at Shandong University, Ministry of Education, PR China) ,  Huang Chuanzhen (National Demonstration Center for Experimental Mechanical Engineering Education, Shandong University, PR China) ,  Shi Zhenyu (Centre for Advanced Jet Engineering Technologies (CaJET), School of Mechanical Engineering, Shandong University, Jinan, 250061, PR China) ,  Shi Zhenyu (Key Laboratory of High-Efficiency and Clean Mechanical Manufacture at Shandong University, Ministry of Education, PR China) ,  Shi Zhenyu (National Demonstration Center for Experimental Mechanical Engineering Education, Shandong University, PR China) ,  Ma Yongsheng (Department of Mechanical Engineering, University of Alberta, Canada) ,  Yao Peng (Centre for Advanced Jet Engineering Technologies (CaJET), School of Mechanical Engineering, Shandong University, Jinan, 250061, PR China) ,  Yao Peng (Key Laboratory of High-Efficiency and Clean Mechanical Manufacture at Shandong University, Ministry of Education, PR China) ,  Yao Peng (National Demonstration Center for Experimental Mechanical Engineering Education, Shandong University, PR China)
資料名： Composites. Part B. Engineering  (Composites. Part B. Engineering)
巻： 198  ページ： Null  発行年： 2020年 
JST資料番号： W0437B  ISSN： 1359-8368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 短時間繊維強化高分子複合材料部品を作製するため,溶融堆積モデリング(FDM)を成功裡に適用した。しかし,マトリックスポリマの本質的に限られた機械的性質のため,FDM-3D印刷用の繊維強化高性能熱可塑性複合材料を開発し,工学的応用を拡大する必要がある。本研究では,FDM-3D印刷短炭素繊維(CF)とガラス繊維(GF)強化高性能PEEK複合材料の可能性を調べた。5wt%,10wt%および15wt%の繊維含有量を有する複合フィラメントを押出プロセスを用いて調製し,微細形態観察によって特性化した。そして,熱特性試験は,純粋なPEEKより良い熱安定性を示した。印刷したCF/GF-PEEK部品の性能評価を,機械的性質,微細構造,表面品質および多孔性を含めて検討した。結果は,PEEKへのCF/GFの添加が,延性のコストで,引張と曲げ強度を著しく強化できることを示した。5wt%の低い繊維含有量は,機械的性質の増加,表面品質の改善,および印刷CF/GF-PEEKの多孔性の低減に役立つ。GF/PEEKは繊維上の異なる表面処理によりCF/PEEKより良好な界面結合を有した。さらに,微細構造観察は,印刷配向に沿って整列した繊維が特性を強化し,一方,細孔が3D印刷CF/GF-PEEKの性能劣化をもたらすことを示唆した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 延性 ,  界面 ,  重合体 ,  表面処理 ,  *印刷 ,  ガラス繊維 ,  炭素繊維 ,  繊維強化 ,  引張 ,  曲げ強さ ,  熱特性 ,  *三次元 ,  *ポリエーテルエーテルケトン ,  PMC【材料】 ,  機械的性質 ,  強度
準シソーラス用語： *三次元印刷 , 【Automatic Indexing@JST】

著者キーワード (4件)： 溶融堆積モデリング ,  耐熱樹脂 ,  繊維強化PEEK複合材料 ,  機械的性質

分類 (2件)： 充填剤,補強材  (YH05030J) ,  機械的性質  (YH02022L)

タイトルに関連する用語 (9件)： Cf ,  強化 ,  PEEK ,  複合材料 ,  フィラメント ,  調製 ,  FDM ,  3D印刷 ,  特性評価