10%TiB_2(p)/Al-5%Cu複合材料の微細構造と腐食挙動に及ぼすLaの影響【JST・京大機械翻訳】

Effect of La on microstructure and corrosion behavior of 10%TiB_2(p)/Al-5%Cu composites

著者 (5件)： Yang Sen (School of Materials Science and Engineering, Inner Mongolia University of Technology, Hohhot 010051, People’s Republic of China) ,  Zhang Ruiying (School of Materials Science and Engineering, Inner Mongolia University of Technology, Hohhot 010051, People’s Republic of China) ,  Liu Huan (School of Materials Science and Engineering, Inner Mongolia University of Technology, Hohhot 010051, People’s Republic of China) ,  Li Jinxuan (School of Materials Science and Engineering, Inner Mongolia University of Technology, Hohhot 010051, People’s Republic of China) ,  Yan Han (School of Materials Science and Engineering, Inner Mongolia University of Technology, Hohhot 010051, People’s Republic of China)
資料名： Journal of Materials Research and Technology  (Journal of Materials Research and Technology)
巻： 9  号： 4  ページ： 7047-7058  発行年： 2020年 
JST資料番号： W3532A  ISSN： 2238-7854  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 10%TiB_2(p)/Al-5%Cu複合材料の微細構造および腐食挙動に及ぼすLaの影響を,コンピュータ支援冷却曲線分析(CA-CCA),X線回折,EDS,SEM,TEMおよび電気化学試験を用いて研究した。実験結果から,La添加は複合材料の凝固速度を低下させ,一次α-Alの核形成温度を低下させ,Al-Cu共晶の変態温度を高め,液体-固体間隔を狭くした。一方,Al_2.12La_0.88相生成は複合材料へのLa添加後に見出され,CuAl_2相の析出はLa含有量の増加とともに減少した。TiB_2クラスタと第2相を含む大きな凝集体の偏析は,Laの添加後に明らかに改善され,複合材料のより均一な微細構造をもたらした。さらに,適切なLaは3.5%の塩化ナトリウム溶液中で10%TiB_2(p)/Al-5%Cu複合材料の耐食性を高めた。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  核形成 ,  共晶 ,  転移温度 ,  偏析 ,  *ランタン ,  耐食性 ,  塩化ナトリウム ,  クラスタ ,  電気化学 ,  凝固速度 ,  CAE【計算機】 ,  凝集体
準シソーラス用語： 冷却曲線 ,  *腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (5件)： - ,  - ,  - ,  - ,  -

分類 (2件)： 機械的性質  (WB02030U) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (5件)： Al ,  複合材料 ,  微細構造 ,  腐食挙動 ,  La