U-0.79wt%Ti合金中のTi(C,N)介在物による強化された水素腐食【JST・京大機械翻訳】

An enhanced hydrogen corrosion by the Ti(C,N) inclusions in U-0.79 wt%Ti alloy

著者 (10件)： Li Fangfang (China Academy of Engineering Physics, Mianyang, 621900, China) ,  Lu Lei (China Academy of Engineering Physics, Mianyang, 621900, China) ,  Meng Xiandong (China Academy of Engineering Physics, Mianyang, 621900, China) ,  Xiao Hong (China Academy of Engineering Physics, Mianyang, 621900, China) ,  Ji Hefei (China Academy of Engineering Physics, Mianyang, 621900, China) ,  Zeng Rongguang (China Academy of Engineering Physics, Mianyang, 621900, China) ,  Zhang Xinjian (China Academy of Engineering Physics, Mianyang, 621900, China) ,  Wang Xiaolin (China Academy of Engineering Physics, Mianyang, 621900, China) ,  Zhao Yawen (China Academy of Engineering Physics, Mianyang, 621900, China) ,  Shi Peng (China Academy of Engineering Physics, Mianyang, 621900, China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 820  ページ： Null  発行年： 2020年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： U-0.79wt%Ti合金中の主介在物の化学組成と微細構造を走査型電子分光法(SAM)と高分解能走査透過型電子顕微鏡(HRSTEM)によって研究した。SAM分析は,U-0.79wt%Ti合金における支配的な介在物がチタン炭窒化物の形であることを示した。HRSTEMは,炭窒化チタン介在物の高分解能原子画像を示し,さらに,チタン炭窒化物介在物の相構造がTi(C,N)であることを検証した。水素攻撃はU-0.79wt%Ti合金中のTi(C,N)介在物の大部分で優先的に起こり,初期水素化物成長は0.6の反応次数で放物線状の速度論的挙動を示した。介在物-酸化物界面は金属に到達する水素の優先輸送チャネルとして作用できる。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 酸化物 ,  高分解能 ,  水素化物 ,  *合金 ,  電子分光法 ,  *チタン合金 ,  *水素 ,  化学組成 ,  *腐食 ,  界面 ,  走査 ,  電子顕微鏡観察 ,  速度論 ,  *介在物 ,  反応次数 ,  チャネル

著者キーワード (6件)： U-0.79wt%Ti合金 ,  介在物 ,  組成 ,  微細構造 ,  水素化物 ,  核形成部位

分類 (2件)： その他の金属組織学  (WB01040Y) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： Ti ,  介在物 ,  強化 ,  水素 ,  腐食