La_2O_3添加による添加剤製造Ti-6.5Al-3.5Mo-1.5Zr-0.3Siチタン合金の結晶粒微細化【JST・京大機械翻訳】

Grain refinement of additive manufactured Ti-6.5Al-3.5Mo-1.5Zr-0.3Si titanium alloy by the addition of La₂O₃

著者 (6件)： Chen Yuanhang (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China) ,  Yang Chunli (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China) ,  Fan Chenglei (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China) ,  Zhuo Yimin (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China) ,  Lin Sanbao (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China) ,  Chen Chao (State Key Laboratory of Advanced Welding and Joining, Harbin Institute of Technology, Harbin 150001, China)
資料名： Materials Letters  (Materials Letters)
巻： 275  ページ： Null  発行年： 2020年 
JST資料番号： E0935A  ISSN： 0167-577X  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本論文では,2つの異なる質量分率を有するLa_2O_3を,ワイヤおよびアーク添加物製造技術によって,Ti-6.5Al-3.5Mo-1.5Zr-0.3Siで合金化した。ミクロ組織の変化と機械的性能に及ぼすLa_2O_3添加の影響を調べた。結果は,La_2O_3添加が事前のβ粒のサイズを著しく微細化できることを示した。La_2O_3添加は,堆積試料中の安定な固体粒子として同定され,不均一核形成を促進した。微細構造のキャラクタリゼーションおよび引張試験は,La_2O_3添加の質量分率の増加とともに,それぞれ10.56mm2から0.52mm2および9.72%から3.32%まで,粒径および伸びが徐々に減少することを示した。脆性固体粒子は破壊しやすく,初期亀裂を与えるので,La_2O_3の添加は延性不良の原因であった。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 延性 ,  機械的性質 ,  亀裂 ,  *合金 ,  引張試験 ,  *チタン合金 ,  脆性 ,  粒径 ,  *結晶粒微細化 ,  合金化 ,  金属線 ,  精密化 ,  固体粒子 ,  生産技術
準シソーラス用語： 不均一核形成 , 【Automatic Indexing@JST】

著者キーワード (6件)： WAAM ,  TC11チタン合金 ,  La_2O_3 ,  金属と合金 ,  微細構造 ,  機械的性質