レーザクラッディングFe基被覆の摩耗特性に関する超音波振動【JST・京大機械翻訳】

Ultrasonic vibration on wear property of laser cladding Fe-based coating

著者 (6件)： Xu Jiale (School of Mechanical Engineering, Jiangsu University, Zhenjiang, People’s Republic of China) ,  Zhou Jianzhong (School of Mechanical Engineering, Jiangsu University, Zhenjiang, People’s Republic of China) ,  Tan Wensheng (Changzhou Key Laboratory of Large Plastic Parts Intelligence Manufacturing, Changzhou College of Information Technology, Changzhou, People’s Republic of China) ,  Huang Shu (School of Mechanical Engineering, Jiangsu University, Zhenjiang, People’s Republic of China) ,  Wang Songtao (School of Mechanical Engineering, Jiangsu University, Zhenjiang, People’s Republic of China) ,  He Wenyuan (School of Mechanical Engineering, Jiangsu University, Zhenjiang, People’s Republic of China)
資料名： Surface Engineering  (Surface Engineering)
巻： 36  号： 12  ページ： 1261-1269  発行年： 2020年 
JST資料番号： A0614C  ISSN： 0267-0844  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： ABSTRACT:Feベースコーティングを,超音波振動によって支援されたレーザクラッディングによって,GCr15軸受鋼上に作製した。クラッド層のミクロ組織の変化と耐摩耗性を系統的に調べた。その結果,エピタキシャル成長柱状結晶粒が散乱し,その後,クラッド層中に形成した多数の微細な等軸結晶を有する異なる方向に成長した。超音波振動支援なしのクラッド層と比較して,ナノ硬度および弾性率は,それぞれ10.54および289.3GPaであり,それぞれ15.7および4.9%増加した。超音波振動の有無によるクラッド層の平均摩擦係数は,それぞれ,0.339と0.382であり,基板(0.416)と比較して,18.5と8.2%減少し,対応する相対摩耗抵抗係数は,基板のそれの47.1と21.4倍であった。クラッド層の耐摩耗性は,基板,特に超音波振動によって作製されたクラッド層のものより良かった。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： エピタクシー ,  抗力係数 ,  耐摩耗性 ,  弾性係数 ,  摩擦係数 ,  塗料 ,  軸受鋼 ,  *被覆 ,  柱状晶 ,  *超音波振動 ,  *レーザクラッディング ,  *摩耗特性
準シソーラス用語： クラッド層 ,  ナノ硬さ , 【Automatic Indexing@JST】

著者キーワード (4件)： レーザクラッディング ,  超音波振動支援 ,  Fe系塗料 ,  耐摩耗性

分類 (2件)： 肉盛  (WC07060N) ,  クラッド材  (WE04020G)

タイトルに関連する用語 (4件)： レーザクラッディング ,  Fe基 ,  摩耗特性 ,  超音波振動