スラリーでアルミニウム化した変形可能なオーステンパ球状黒鉛鋳鉄(DAI)の高温酸化【JST・京大機械翻訳】

High Temperature Oxidation of Slurry Aluminized Deformable Austempered Ductile Iron (DADI)

著者 (5件)： Tsurtsumia Olga (Republic Center for Structure Research, Georgian Technical University, Tbilisi, Georgia) ,  Pedraza Fernando (Laboratoire des Sciences de l’Ingenieur pour l’Environnement (LaSIE UMR-CNRS 7356), Universite de La Rochelle, La Rochelle Cedex 1, France) ,  Gregoire Benjamin (Laboratoire des Sciences de l’Ingenieur pour l’Environnement (LaSIE UMR-CNRS 7356), Universite de La Rochelle, La Rochelle Cedex 1, France) ,  Khidasheli Nugzar (Republic Center for Structure Research, Georgian Technical University, Tbilisi, Georgia) ,  Kutelia Elguja (Republic Center for Structure Research, Georgian Technical University, Tbilisi, Georgia)
資料名： Metallurgical and Materials Transactions. A. Physical Metallurgy and Materials Science  (Metallurgical and Materials Transactions. A. Physical Metallurgy and Materials Science)
巻： 51  号： 2  ページ： 920-926  発行年： 2020年 
JST資料番号： E0265B  ISSN： 1073-5623  CODEN： MTTABN  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本研究は,新しいクラスの鋳鉄(変形性オーステンパ延性鉄,DADI)のアルミニウム化と酸化挙動について報告する。スラリーのアルミニウム化は,基板のグラファイト介在物への溶融アルミニウムの濡れ性の欠如により,不均一な被覆をもたらした。これにもかかわらず,空気中650°Cで100時間の等温試験は,被覆無しで形成された非常に保護されていない酸化鉄と比較して,混合Al含有スピネルの形成に関連した酸素取り込みの劇的な減少を明らかにした。それは,例えばニッケルの前被覆によるより厚いアルミナイド層の堆積が,さらなるDADI鋳鉄を保護する有望な方法であることを誘導する。Copyright 2019 The Minerals, Metals & Materials Society and ASM International Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 酸化鉄 ,  濡れ ,  *オーステンパ ,  グラファイト ,  スラリー ,  *高温酸化 ,  酸素 ,  *アルミニウム ,  ニッケル ,  スピネル ,  被覆 ,  *鋳鉄 ,  *球状黒鉛鋳鉄 ,  介在物
準シソーラス用語： アルミナイド , 【Automatic Indexing@JST】

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  鋳造に関する各種技術  (WC01040B)

タイトルに関連する用語 (4件)： スラリー ,  アルミニウム ,  オーステンパ球状黒鉛鋳鉄 ,  高温酸化