Ti_42Al_5Mn合金におけるFe/W/Mo添加により誘起されたLaves相の勾配特性析出挙動への洞察【JST・京大機械翻訳】

Insights into the gradient-characteristic precipitation behaviors of laves phase induced by Fe/W/Mo addition in Ti42Al5Mn alloy

著者 (18件)： Tang Hongjian (Shi-Changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016, China) ,  Tang Hongjian (School of Materials Science and Engineering, University of Science and Technology of China, Hefei, 230026, China) ,  Xing Weiwei (Shi-Changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016, China) ,  Xing Weiwei (CAS Key Laboratory of Nuclear Materials and Safety Assessment, IMR (NMSA), Shenyang, 110014, China) ,  Li Xiaobing (Shi-Changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016, China) ,  Li Xiaobing (CAS Key Laboratory of Nuclear Materials and Safety Assessment, IMR (NMSA), Shenyang, 110014, China) ,  Chen Bo (Shi-Changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016, China) ,  Chen Bo (CAS Key Laboratory of Nuclear Materials and Safety Assessment, IMR (NMSA), Shenyang, 110014, China) ,  Zhao Pengxiang (Shi-Changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016, China) ,  Zhao Pengxiang (School of Materials Science and Engineering, University of Science and Technology of China, Hefei, 230026, China) ,  Shu Lei (Shi-Changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016, China) ,  Shu Lei (CAS Key Laboratory of Nuclear Materials and Safety Assessment, IMR (NMSA), Shenyang, 110014, China) ,  Zhang Mengshu (Shi-Changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016, China) ,  Zhang Mengshu (CAS Key Laboratory of Nuclear Materials and Safety Assessment, IMR (NMSA), Shenyang, 110014, China) ,  Ma Yingche (Shi-Changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016, China) ,  Ma Yingche (CAS Key Laboratory of Nuclear Materials and Safety Assessment, IMR (NMSA), Shenyang, 110014, China) ,  Liu Kui (Shi-Changxu Innovation Center for Advanced Materials, Institute of Metal Research, Chinese Academy of Sciences, Shenyang, 110016, China) ,  Liu Kui (CAS Key Laboratory of Nuclear Materials and Safety Assessment, IMR (NMSA), Shenyang, 110014, China)
資料名： Intermetallics  (Intermetallics)
巻： 128  ページ： Null  発行年： 2021年 
JST資料番号： W0672A  ISSN： 0966-9795  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 使用温度規則β相(β_o)では,新しいβ凝固γ-TiAl合金における(メタ)安定相は,予想外の相変態手順を受け,それは,優勢な組成に強く依存する。本研究では,β_o領域からのLaves相の析出挙動に及ぼすFe,WおよびMoとの合金化の影響およびMn含有β凝固γ-TiAl合金の等温焼鈍中の同時元素再分布を系統的に調べた。Electron顕微鏡分析は,Laves相の形成がFeによって促進されるが,Wによってある程度遅れるという証拠を提供する。鋭いコントラストにおいて,Moとの合金化はβ_o→α_2変態の集中的な拘束によりLaves相の析出を効果的に抑制できることを確認した。さらに,相安定性に及ぼす合金元素の影響を理論計算によって注意深く評価し,WまたはMoの存在下でLaves相の熱力学的不安定化を明らかにし,一方,Laves相はFeによってエネルギー的に安定化し,これは実験結果と良好な一致を示した。さらに,古典的DSC評価は,Laves相の生成に関する熱事象と析出速度のより良い理解をサポートするために補足された。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 凝固 ,  金属間化合物 ,  *合金 ,  コントラスト ,  熱力学 ,  *鉄 ,  *モリブデン ,  合金元素 ,  *Laves相 ,  β相 ,  合金化 ,  再分布
準シソーラス用語： 理論計算 ,  析出速度 ,  等温焼なまし , 【Automatic Indexing@JST】

著者キーワード (6件)： TiAl系金属間化合物 ,  Laves相 ,  降水 ,  拡散 ,  第一原理計算 ,  DSC

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  組織的硬化現象  (WB01020C)

タイトルに関連する用語 (8件)： Fe ,  Mo ,  誘起 ,  Laves相 ,  勾配 ,  析出 ,  挙動 ,  洞察