AlリッチAl-Ce-Mn合金における三元化合物の一次凝固【JST・京大機械翻訳】

Primary solidification of ternary compounds in Al-rich Al-Ce-Mn alloys

著者 (8件)： Yang Y. (Materials Science and Technology Division, Oak Ridge National Lab, Oak Ridge, TN, 37831, USA) ,  Bahl S. (Materials Science and Technology Division, Oak Ridge National Lab, Oak Ridge, TN, 37831, USA) ,  Sisco K. (University of Tennessee-Knoxville, Knoxville, TN, 37996, USA) ,  Lance M. (Materials Science and Technology Division, Oak Ridge National Lab, Oak Ridge, TN, 37831, USA) ,  Shin D. (Materials Science and Technology Division, Oak Ridge National Lab, Oak Ridge, TN, 37831, USA) ,  Shyam A. (Materials Science and Technology Division, Oak Ridge National Lab, Oak Ridge, TN, 37831, USA) ,  Plotkowski A. (Materials Science and Technology Division, Oak Ridge National Lab, Oak Ridge, TN, 37831, USA) ,  Dehoff R.R. (Materials Science and Technology Division, Oak Ridge National Lab, Oak Ridge, TN, 37831, USA)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 844  ページ： Null  発行年： 2020年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 三元化合物Al_20Mn_2CeとAl_10Mn_2Ceの一次凝固を,熱力学モデリングと古典的核形成理論の結合を通して解析した。Al_20Mn_2CeとAl_10Mn_2Ceの熱力学モデルを,第一原理計算エンタルピーと本研究と文献から得られた実験データに基づくCALPHAD法を用いて開発した。分析は,Al_10Mn_2Ceの核形成に対する大きな熱力学的駆動力にもかかわらず,その小さな界面エネルギーのため,高度に過冷却した液体中のAl_20Mn_2Ce相に対して核形成が優先されることを示唆した。したがって,急速冷却速度による製造法はAlリッチAl-Ce-Mn合金に対するAl_20Mn_2Ceの一次凝固に有利である。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： エンタルピー ,  核形成 ,  過冷却 ,  *凝固 ,  熱力学 ,  表面エネルギー ,  熱力学模型 ,  高速冷却 ,  駆動力
準シソーラス用語： CALPHAD法 ,  第一原理計算 , 【Automatic Indexing@JST】

著者キーワード (4件)： 一次凝固 ,  熱力学 ,  核形成 ,  Al-Mn-Ce合金

分類 (2件)： 金属系の相平衡・状態図  (CB03012T) ,  変態組織,加工組織  (WB01030N)

タイトルに関連する用語 (4件)： Al ,  Ce ,  Mn合金 ,  凝固