硬化鋼の機械加工における表面健全性のレビュー【JST・京大機械翻訳】

A review of surface integrity in machining of hardened steels

著者 (6件)： Sales Wisley F. (Federal University of Uberlandia (UFU), Faculty of Mechanical Engineering, Uberlandia, MG, Brazil) ,  Schoop Julius (University of Kentucky, Institute for Sustainable Manufacturing (ISM), Lexington, KY, USA) ,  da Silva Leonardo R.R. (Federal University of Uberlandia (UFU), Faculty of Mechanical Engineering, Uberlandia, MG, Brazil) ,  Machado Alisson R. (Federal University of Uberlandia (UFU), Faculty of Mechanical Engineering, Uberlandia, MG, Brazil) ,  Machado Alisson R. (Mechanical Engineering Graduate Program, Pontificia Universidade Catolica do Parana - PUCPR, Curitiba, PR, CEP: 80215-901, Brazil) ,  Jawahir I.S. (University of Kentucky, Institute for Sustainable Manufacturing (ISM), Lexington, KY, USA)
資料名： Journal of Manufacturing Processes  (Journal of Manufacturing Processes)
巻： 58  ページ： 136-162  発行年： 2020年 
JST資料番号： W3312A  ISSN： 1526-6125  資料種別： 逐次刊行物 (A)
記事区分： 文献レビュー  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 圧延ダイス,金型,軸受,軸,歯車,その他に45HR_Cより通常硬い硬化鋼の加工における表面健全性の背景を,低チップ-工具接触面積と高力を促進し,次に高い接触応力と高温をもたらす機械的と物理的特性の組み合わせによって切断するのが困難と考えられる。特に,新しく機械加工した工作物表面に生成した高温は,白色層や微小亀裂,ワーピングなどの貧弱な表面完全性を促進し,その結果,疲れ強さを低下させた。さらに,工具摩耗は,しばしば顕著であり,さらに,高い切削温度の問題を悪化させ,品質管理中のハード加工部品の頻繁な拒絶をもたらし,従って,製造コストを増加させる。本研究では,硬化鋼の加工時の表面完全性の背景を紹介し,文献からの主な課題とその解決策を,多様な事例研究に基づいて考察した。芸術の状態に基づいて,硬化鋼の加工誘起表面健全性の分野における今後の方向に関する展望に加えて,一連の結論と最良の実践を示した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 高温 ,  残留応力 ,  品質管理 ,  製造原価 ,  軸受 ,  工具摩耗 ,  圧延 ,  *機械工作 ,  疲れ強さ ,  *焼入鋼 ,  事例研究 ,  接触応力 ,  微小亀裂
準シソーラス用語： 接触面積 ,  白色層 , 【Automatic Indexing@JST】

著者キーワード (6件)： 表面完全性 ,  焼入鋼 ,  白層 ,  残留応力 ,  粗さ ,  切削油