Fatigue life assessment of Al-steel resistance spot welds using the maximum principal strain approach considering material inhomogeneity

著者 (7件)： Shi Liting (CanmetMATERIALS, 183 Longwood Road South, Hamilton, Ontario L9P 0A5, Canada) ,  Shi Liting (School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China) ,  Kang Jidong (CanmetMATERIALS, 183 Longwood Road South, Hamilton, Ontario L9P 0A5, Canada) ,  Gesing Mark (CanmetMATERIALS, 183 Longwood Road South, Hamilton, Ontario L9P 0A5, Canada) ,  Chen Xu (School of Chemical Engineering and Technology, Tianjin University, Tianjin 300072, China) ,  Haselhuhn Amberlee S. (General Motors Global R&D Center, 30470 Harley Earl Blvd, Warren, MI 48092, USA) ,  Carlson Blair E. (General Motors Global R&D Center, 30470 Harley Earl Blvd, Warren, MI 48092, USA)
資料名： International Journal of Fatigue  (International Journal of Fatigue)
巻： 140  ページ： Null  発行年： 2020年 
JST資料番号： D0802B  ISSN： 0142-1123  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 新しいマルチリングドーム電極を用いて,種々のAl-AlおよびAl-鋼抵抗スポット溶接(RSW)について,大きな疲れ試験プログラムを実施した。結果は,疲れ寿命が溶接ナゲット直径と板厚だけでなく,アルミニウムシートの塑性変形によっても影響を受けるという仮説を支持する。RSWにおける材料不均一性を考慮した有限要素モデルを開発し,最大主歪を決定した。結果は,異なるシート厚さまたは材料組合せを有するスタックアップに対して,最大主歪が,材料不均一性を考慮した場合,疲労寿命とより良い相関を示した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 疲れ試験 ,  *アルミニウム ,  *鋼 ,  応力法 ,  塑性変形 ,  *疲れ寿命 ,  不均一性 ,  板厚
準シソーラス用語： *抵抗点溶接 ,  FEMモデル ,  *主歪 ,  溶接ナゲット ,  アルミニウムシート , 【Automatic Indexing@JST】

著者キーワード (5件)： 抵抗スポット溶接 ,  疲れ寿命評価 ,  構造応力法 ,  最大主歪法 ,  材料不均一性

分類 (2件)： 金属材料  (HC05020S) ,  溶接設計,溶接構造物  (WC07140A)

タイトルに関連する用語 (6件)： 不均一性 ,  主歪 ,  Al ,  抵抗スポット溶接 ,  疲れ寿命 ,  評価