Al-Mg合金と低炭素鋼間の異種継手の水中摩擦撹拌溶接:熱機械的モデリング,微細構造特性,機械的性質【JST・京大機械翻訳】

Submerged friction stir welding of dissimilar joints between an Al-Mg alloy and low carbon steel: Thermo-mechanical modeling, microstructural features, and mechanical properties

著者 (4件)： Aghajani Derazkola Hamed (Young Researchers and Elites Club, Science and Research Branch, Islamic Azad University, Tehran, Iran) ,  Eyvazian Arameh (Department of Mechanical and Industrial Engineering, Qatar University, Doha, Qatar) ,  Simchi Abdolreza (Department of Materials Science and Engineering, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, 14588 Tehran, Iran) ,  Simchi Abdolreza (Institute for Nanoscience and Nanotechnology, Sharif University of Technology, P.O. Box 11365-9466, Azadi Avenue, 14588 Tehran, Iran)
資料名： Journal of Manufacturing Processes  (Journal of Manufacturing Processes)
巻： 50  ページ： 68-79  発行年： 2020年 
JST資料番号： W3312A  ISSN： 1526-6125  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 突合せ継手構成におけるAl-Mg合金(AA5005)と低炭素鋼(ASTM A283)の水中異種摩擦撹拌溶接を研究した。継手の機械的及び冶金的性質に及ぼす273,298及び333Kの3水準での浸漬温度の影響を調べた。空気処理試験片と比較して,浸漬異種継手の特性の改善を示した。この改善は,媒体の冷却効果により引き起こされたピーク温度の低下と微細粒構造のためであることを実証した。しかし,加熱水での処理はより良い表面品質をもたらすが,材料の表面流は空気処理試料でより滑らかである。また,界面の厚さは,水中摩擦撹拌溶接によって減少した。異種継手の強度は,アルミニウム合金と鋼のそれぞれ62~72%と19~23%の間で変化する。水中での処理により改善できる水中溶接において,より低い硬度を達成した。本研究の結果は,加工環境の温度を制御することにより,異種継手のロバストな摩擦撹拌溶接の道を開く可能性がある。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *低炭素鋼 ,  *合金 ,  ロバスト性 ,  *機械的性質 ,  浸漬 ,  *鋼 ,  海洋構造物 ,  界面 ,  硬度 ,  *摩擦撹拌溶接 ,  冶金 ,  媒質 ,  水中溶接 ,  アルミニウム合金 ,  表面流

著者キーワード (5件)： 水中溶接 ,  固相接合 ,  異種材料 ,  冶金学的性質 ,  海洋構造物

分類 (3件)： 溶接技術  (WC07030G) ,  溶接部  (WC07100I) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (9件)： Al-Mg合金 ,  低炭素鋼 ,  継手 ,  水中 ,  摩擦撹拌溶接 ,  モデリング ,  微細 ,  構造特性 ,  機械的性質