MIM技術のためのアンバ合金の構造と特性【JST・京大機械翻訳】

Structure and properties of invar alloys for MIM technologies

著者 (9件)： Kulkov S N (National Research Tomsk State University, Tomsk, Russia) ,  Kulkov S N (Institute of Strength Physics and Materials Science SB RAS, Tomsk, Russia) ,  Kulkov S N (National Research Tomsk Polytechnic University, Tomsk, Russia) ,  Abdulmenova E V (Institute of Strength Physics and Materials Science SB RAS, Tomsk, Russia) ,  Abdulmenova E V (National Research Tomsk Polytechnic University, Tomsk, Russia) ,  Shadrin V S (National Research Tomsk State University, Tomsk, Russia) ,  Leonov A A (National Research Tomsk Polytechnic University, Tomsk, Russia) ,  Leonov A A (Institute of High Current Electronics SB RAS, Tomsk, Russia) ,  Levkov R V (National Research Tomsk Polytechnic University, Tomsk, Russia)
資料名： IOP Conference Series: Materials Science and Engineering  (IOP Conference Series: Materials Science and Engineering)
巻： 696  号： 1  ページ： 012005 (4pp)  発行年： 2019年 
JST資料番号： W5559A  ISSN： 1757-8981  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本論文は,粉末混合物から焼結により得られたFe-Ni合金を研究した。30~40wt.Niをパラフィン及びワックス結合剤と混合し,次いでプレスし,1300°Cで1時間焼結した。粉末混合物の焼結後,面心立方格子(γ相)と体心立方格子(α相)が形成されることを示した。α相の含有量は,粉末混合物中のNi濃度が30から35wt.%Niに増加すると,37%から2%に減少した。γ相の平均粒径は26.5±12.3μmから18.3±9.1μmに減少し,試料の気孔率は13±1.4%から18.4±1.1%に増加した。γ相の格子定数は3.5849から10~10mから3.597まで増加し,良く知られたinvar合金に対応する。焼結試料の微小硬さの最大値は1.04±0.07GPaであった。したがって,FeとNi粉末混合物の焼結によって得られた合金は,鋳造合金の典型的な特性を持っている。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *合金 ,  鉄 ,  γ相 ,  格子定数 ,  パラフィンワックス ,  *アンバ ,  ワックス ,  α相 ,  焼結 ,  ニッケル ,  微小硬さ ,  空隙率
準シソーラス用語： 鋳造合金 ,  体心立方格子 ,  面心立方格子 , 【Automatic Indexing@JST】