高性能硬質被覆用の新しい多層ダイヤモンド/β-SiC複合材料構造【JST・京大機械翻訳】

New multilayered diamond/β-SiC composite architectures for high-performance hard coating

著者 (16件)： Yuan Ziyao (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Wenhua Road 72, Shenyang, 110016, China) ,  Yuan Ziyao (School of Materials Science and Engineering, University of Science and Technology of China, Wenhua Road 72, Shenyang, 110016, China) ,  Guo Yuning (Institute of Materials Engineering, University of Siegen, Paul-Bonatz-Str. 9-11, Siegen, 57076, Germany) ,  Li Cuihong (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Wenhua Road 72, Shenyang, 110016, China) ,  Liu Lusheng (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Wenhua Road 72, Shenyang, 110016, China) ,  Yang Bing (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Wenhua Road 72, Shenyang, 110016, China) ,  Song Haozhe (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Wenhua Road 72, Shenyang, 110016, China) ,  Zhai Zhaofeng (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Wenhua Road 72, Shenyang, 110016, China) ,  Zhai Zhaofeng (School of Materials Science and Engineering, University of Science and Technology of China, Wenhua Road 72, Shenyang, 110016, China) ,  Lu Zhigang (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Wenhua Road 72, Shenyang, 110016, China) ,  Lu Zhigang (School of Materials Science and Engineering, University of Science and Technology of China, Wenhua Road 72, Shenyang, 110016, China) ,  Li Hong (Guangdong Institute of New Materials, Changxing Road 363, Tianhe District, Guangzhou, 510650, China) ,  Staedler Thorsten (Institute of Materials Engineering, University of Siegen, Paul-Bonatz-Str. 9-11, Siegen, 57076, Germany) ,  Huang Nan (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Wenhua Road 72, Shenyang, 110016, China) ,  Jiang Xin (Shenyang National Laboratory for Materials Science, Institute of Metal Research, Chinese Academy of Sciences, Wenhua Road 72, Shenyang, 110016, China) ,  Jiang Xin (Institute of Materials Engineering, University of Siegen, Paul-Bonatz-Str. 9-11, Siegen, 57076, Germany)
資料名： Materials & Design  (Materials & Design)
巻： 186  ページ： Null  発行年： 2020年 
JST資料番号： A0495B  ISSN： 0264-1275  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 被覆構造の設計は硬質被覆の機械的性能の改善に重要な役割を果たす。本研究では,いくつかの新しい多層ダイヤモンド/β-SiC複合材料構造を,ホットフィラメント化学蒸着により超硬合金基板上に堆積した。電界放出型走査電子顕微鏡(FE-SEM)観察は,ダイヤモンド/β-SiC複合層と微結晶ダイヤモンド(MCD)またはナノ結晶ダイヤモンド(NCD)層を有する周期的多層構造を明らかにした。さらに,Rockwell押込み,引かきおよびナノインデンテーション試験は,多層ダイヤモンド/β-SiC複合材料およびMCD被覆が,すべての堆積したままの被覆の間で,良好な接着(52.9±0.5N)および亀裂伝搬抵抗を有するだけでなく,高硬度(83.6±3.5GPa)および弾性率(856.1±87.5GPa)を有することを示した。この構成に対して,被覆の硬度はMCD層から継承され,一方,低い残留応力,強化された接着および亀裂伝搬抵抗は複合被覆および多層構造によるものである。したがって,ダイヤモンド被覆の機械的性質は,革新的なダイヤモンド/β-SiC複合材料多層によって改善され,高性能ダイヤモンド被覆切削工具のための潜在的アプローチを提供する。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *ダイヤモンド ,  硬質 ,  多層構造 ,  *被覆 ,  機械的性質 ,  多層 ,  化学蒸着 ,  複合材料 ,  亀裂伝搬 ,  弾性係数 ,  微結晶 ,  残留応力 ,  接着 ,  超硬合金 ,  *炭化ケイ素

著者キーワード (5件)： ダイヤモンド/β-SiC ,  複合材料 ,  多層 ,  接着 ,  硬さ

分類 (2件)： 金属系複合材料一般  (WE04010V) ,  その他の物理的・機械的性質  (WB02040F)

タイトルに関連する用語 (6件)： 高性能 ,  硬質 ,  多層 ,  ダイヤモンド ,  SiC ,  複合材料