付加製造に起因する確率的幾何学的欠陥を持つ格子構造の機械的応答に関する圧縮実験と数値評価【JST・京大機械翻訳】

Compression experiment and numerical evaluation on mechanical responses of the lattice structures with stochastic geometric defects originated from additive-manufacturing

著者 (15件)： Cao Xiaofei (Beijing Key Laboratory of Lightweight Multi-functional Composite Materials and Structures, Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Cao Xiaofei (State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Jiang Yongbo (Beijing Key Laboratory of Lightweight Multi-functional Composite Materials and Structures, Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Jiang Yongbo (State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Zhao Tian (Beijing Key Laboratory of Lightweight Multi-functional Composite Materials and Structures, Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Wang Panding (Beijing Key Laboratory of Lightweight Multi-functional Composite Materials and Structures, Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Wang Yongzhen (Beijing Key Laboratory of Lightweight Multi-functional Composite Materials and Structures, Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Chen Zihao (Beijing Key Laboratory of Lightweight Multi-functional Composite Materials and Structures, Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Chen Zihao (State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Li Ying (Beijing Key Laboratory of Lightweight Multi-functional Composite Materials and Structures, Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Li Ying (State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Xiao Dengbao (Beijing Key Laboratory of Lightweight Multi-functional Composite Materials and Structures, Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Xiao Dengbao (State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Fang Daining (Beijing Key Laboratory of Lightweight Multi-functional Composite Materials and Structures, Institute of Advanced Structure Technology, Beijing Institute of Technology, Beijing, 100081, China) ,  Fang Daining (State Key Laboratory of Explosion Science and Technology, Beijing Institute of Technology, Beijing, 100081, China)
資料名： Composites. Part B. Engineering  (Composites. Part B. Engineering)
巻： 194  ページ： Null  発行年： 2020年 
JST資料番号： W0437B  ISSN： 1359-8368  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 加成的製造プロセスは一般的に,設計されたままの対応物から離れた形状を持つ格子を作り,作製した格子試料内にいくつかの固有の幾何学的不完全性が存在する。本論文では,付加製造に起因する確率的幾何学的欠陥を有する格子構造の機械的応答を調べた。ここでは,X線コンピュータ断層撮影(CT)を用いて,準静的圧縮下での弾性応答,損傷開始および破壊進展におけるそれらの役割を研究するために,プロセス誘起欠陥の形態および分布を把握した。試験結果は,より多くの幾何学的不完全性が対角または垂直支柱より水平支柱に存在することを示した。次に,X線CT画像から抽出し,統計的FEモデルを確立するための理想的有限要素(FE)モデルに,プロセス誘起欠陥(すなわち,支柱多孔性,ストラット厚さ変化およびストラット波形)を導入した。統計的FEモデル予測結果と実験結果の間にはより多くの一致が観察された。最後に,格子の機械的応答とエネルギー吸収に及ぼす単一幾何学的欠陥の役割を調べた。格子構造における支柱の厚さの変化は,ストラットの空隙率やストラットのうねりよりもエネルギー吸収に大きな影響を及ぼすことが示された。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *格子構造 ,  弾性 ,  多孔性 ,  支柱 ,  空隙率 ,  生産工程 ,  計算機トモグラフィー ,  エネルギー吸収 ,  *付加製造
準シソーラス用語： 変形モード ,  FEMモデル ,  有限要素 ,  *機械的応答 ,  X線CT画像 , 【Automatic Indexing@JST】