高分子/ナノダイヤモンド複合材料の強化された機械的性質のためのデトネーションナノダイヤモンドの表面最適化【JST・京大機械翻訳】

Surface optimization of detonation nanodiamonds for the enhanced mechanical properties of polymer/nanodiamond composites

著者 (19件)： Khan Muhammad (Department of Chemistry, University of Okara, Punjab, Pakistan) ,  Khan Muhammad (School of Materials Science and Engineering, Northwestern Polytechnical University, Xian 710072, PR China) ,  Khan Muhammad (NPU-NCP Joint International Research Center on Advanced Nanomaterials and Defects Engineering, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, PR China) ,  Hamid Abdul (Department of Chemistry, University of Okara, Punjab, Pakistan) ,  Tiehu Li (School of Materials Science and Engineering, Northwestern Polytechnical University, Xian 710072, PR China) ,  Tiehu Li (NPU-NCP Joint International Research Center on Advanced Nanomaterials and Defects Engineering, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, PR China) ,  Zada Amir (Department of Chemistry, Abdul Wali Khan University Mardan, 23200, Pakistan) ,  Attique Faisal (Department of Chemistry, University of Okara, Punjab, Pakistan) ,  Ahmad Naveed (Department of Chemistry, University of Okara, Punjab, Pakistan) ,  Ullah Azeem (School of Materials Science and Engineering, Northwestern Polytechnical University, Xian 710072, PR China) ,  Ullah Azeem (NPU-NCP Joint International Research Center on Advanced Nanomaterials and Defects Engineering, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, PR China) ,  Hayat Asif (School of Chemistry, Fuzhou University, PR China) ,  Mahmood Iram (Department of Industrial Engineering, King Khalid University Abha 61413, Saudi Arabia) ,  Hussain Amjad (Department of Chemistry, University of Okara, Punjab, Pakistan) ,  Khan Yaqoob (NPU-NCP Joint International Research Center on Advanced Nanomaterials and Defects Engineering, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, PR China) ,  Ahmad Ishaq (NPU-NCP Joint International Research Center on Advanced Nanomaterials and Defects Engineering, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, PR China) ,  Ali Amjad (Department of Chemistry, University of Okara, Punjab, Pakistan) ,  Zhao Ting Kai (School of Materials Science and Engineering, Northwestern Polytechnical University, Xian 710072, PR China) ,  Zhao Ting Kai (NPU-NCP Joint International Research Center on Advanced Nanomaterials and Defects Engineering, Northwestern Polytechnical University, Xi’an 710072, Shaanxi, PR China)
資料名： Diamond and Related Materials  (Diamond and Related Materials)
巻： 107  ページ： Null  発行年： 2020年 
JST資料番号： W0498A  ISSN： 0925-9635  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 凝集ナノダイヤモンド(ND)粒子の表面を,UV/オゾンおよびボールミル処理法を用いて,それぞれカルボン酸およびアンミン部分で修飾した。微細構造解析は,初期凝集NDsクラスタが,UV/オゾンとボールミル処理により,サイズで主に減少することを明らかにした。UV/オゾンおよびボールミル官能化NDsを,エタノール,水およびジメチルスルホキシド(DMSO)溶媒への観察の下で分散のために維持した。分散画像は,全ての表面改質NDs試料が,元のNDsと比較して,良好な分散傾向を示すが,ボールミル処理したNDsは,すべてのサンプルよりも,顕著な分散挙動を示した。さらに,機械的性質を,エポキシマトリックスにおける種々の量の表面改質NDを用いて調査した。機械的性質を極限引張強度(UTS),パーセント破断歪および曲げ強度に関してチェックした。上述の全ての機械的性質の結果は,0.3wt%が最高の特性を得るための最適量であることを明らかにした。同様に,ボールミル処理したNDsは,無処理およびUV/オゾン処理ND試料と比較して,全ての機械的性能の顕著な増強を示した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 機械的性質 ,  凝集 ,  *最適化 ,  *デトネーション ,  エポキシ樹脂 ,  オゾン ,  オゾン処理 ,  カルボン酸 ,  *高分子 ,  クラスタ ,  引張強さ ,  官能化 ,  脂肪族アルコール
準シソーラス用語： *ナノダイヤモンド ,  破壊歪 , 【Automatic Indexing@JST】

著者キーワード (5件)： ナノダイヤモンド ,  官能化 ,  ボールミリング ,  エポキシ樹脂 ,  分散と機械的性質

分類 (1件)： 炭素とその化合物  (YB02060D)

物質索引 (1件)： エタノール

タイトルに関連する用語 (6件)： 高分子 ,  ナノダイヤモンド ,  複合材料 ,  強化 ,  機械的性質 ,  最適化