高速走査熱量測定を用いたポリ(L-ラクチド)の研究【JST・京大機械翻訳】

Study of poly(L-lactide) using Fast Scanning Calorimetry

著者 (4件)： Arbeiter Daniela (Institute for Biomedical Engineering, Rostock University Medical Center, Rostock, Friedrich-Barnewitz-Str. 4, 18119 Rostock- Warnemuende, Germany) ,  Oschatz Stefan (Institute for Biomedical Engineering, Rostock University Medical Center, Rostock, Friedrich-Barnewitz-Str. 4, 18119 Rostock- Warnemuende, Germany) ,  Illner Sabine (Institute for Biomedical Engineering, Rostock University Medical Center, Rostock, Friedrich-Barnewitz-Str. 4, 18119 Rostock- Warnemuende, Germany) ,  Grabow Niels (Institute for Biomedical Engineering, Rostock University Medical Center, Rostock, Friedrich-Barnewitz-Str. 4, 18119 Rostock- Warnemuende, Germany)
資料名： Current Directions in Biomedical Engineering (Web)  (Current Directions in Biomedical Engineering (Web))
巻： 6  号： 3  ページ： 422-425  発行年： 2020年 
JST資料番号： U7969A  ISSN： 2364-5504  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 高速走査熱量測定(FSC)は,重合体の熱特性を特性化するための有効な分析ツールである。100000K/sまでの加熱速度は,従来の熱量計にアクセスできない時間スケールでの研究を可能にし,その速度は典型的に約0.5K/s未満である。最近の研究は,チップベースFSCを用いた高分子試料の熱特性の定量的分析を得るための方法を成功裏に示した。したがって,粒子や不織布のような非常に小さい試料サイズを特性化できる。本研究では,標準DSC法の結果と比較して,FSCによるポリ(L-ラクチド)PLLAの熱特性を調べた。PLLA試験片を溶液キャスティングとニードルエレクトロスピニングにより作製した。結果は,PLLAの融解温度に及ぼす加熱速度の顕著な影響を示唆する。結果は,異なる製造方法が結晶性の変化をもたらし,FSC結果が標準DSC測定と完全には比較できないことを示した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 結晶化 ,  重合体 ,  *熱量測定 ,  不織布 ,  融点 ,  高分子 ,  結晶度 ,  定量的分析 ,  加熱速度 ,  熱特性 ,  キャラクタリゼーション ,  示差走査熱量測定 ,  エレクトロスピニング

著者キーワード (5件)： FSC ,  チップセンサ ,  半結晶性PLLA ,  結晶化 ,  融解

分類 (3件)： 高分子固体の構造と形態学  (CG02022M) ,  熱量測定,熱量計  (AD06030G) ,  高分子固体の物理的性質  (CG02024U)

タイトルに関連する用語 (3件)： 熱量測定 ,  L-ラクチド ,  研究