三成分混合ポルトランドセメント-スラグ-シリカヒュームの微細構造と自己収縮に及ぼすCaO取り込みの影響【JST・京大機械翻訳】

Effect of CaO incorporation on the microstructure and autogenous shrinkage of ternary blend Portland cement-slag-silica fume

著者 (4件)： Seo Joonho (Department of Civil and Environmental Engineering, Korea Advanced Institute of Science and Technology, 291 Daehak-ro, Yuseong-gu, Daejeon 34141, South Korea) ,  Park Solmoi (Department of Civil Engineering, Pukyong National University, 45 Yongso-ro, Nam-gu, Busan 48513, South Korea) ,  Yoon H.N. (Department of Civil and Environmental Engineering, Korea Advanced Institute of Science and Technology, 291 Daehak-ro, Yuseong-gu, Daejeon 34141, South Korea) ,  Lee H.K. (Department of Civil and Environmental Engineering, Korea Advanced Institute of Science and Technology, 291 Daehak-ro, Yuseong-gu, Daejeon 34141, South Korea)
資料名： Construction and Building Materials  (Construction and Building Materials)
巻： 249  ページ： Null  発行年： 2020年 
JST資料番号： T0560A  ISSN： 0950-0618  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,三成分混合ポルトランドセメント-スラグ-シリカヒュームの微細構造と自己収縮に及ぼすCaO組込みの影響を調べた。CaO添加量を変えて0.25の水対バインダー比を有する試料を調製し,それらの特性を圧縮強度試験,MIP,XRD,SEM,TGA及び自己収縮により調べた。結果は,取り込まれたCaOがバインダ材料の反応を促進し,それによって初期の圧縮強度を強化することを示した。さらに,組み込まれたCaOの水和で生じる体積変化は,内部剛性骨格の形成中に初期の自己収縮を補償し,最終段階での収縮運動の著しい減少を示した。一方,試料の微細構造と対応する圧縮強度は,CaO取り込みによるマトリックスの過剰な体積膨張のために,水蒸気硬化条件によって著しく影響された。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 微細構造 ,  *スラグ ,  剛性 ,  *ポルトランドセメント ,  水和 ,  圧縮強さ ,  キャラクタリゼーション ,  *シリカヒューム
準シソーラス用語： 自己収縮 ,  体積変化 ,  体積膨張 ,  圧縮強度試験 ,  添加量 ,  バインダ材 , 【Automatic Indexing@JST】