著者 (13件)： Khan Imran Ullah (Advanced Membrane Technology Research Centre (AMTEC), School of Chemical and Energy Engineering, Faculty of Engineering, Universiti Teknologi Malaysia, 81310, Skudai, Johor, Malaysia) ,  Khan Imran Ullah (School of Chemical and Material Engineering (SCME), National University of Science and Technology (NUST), Sector H-12 (44000), Islamabad, Pakistan) ,  Khan Imran Ullah (Process System Engineering Centre (PROSPECT), School of Chemical and Energy Engineering, Faculty of Engineering, Universiti Teknologi Malaysia, 81310, Skudai, Johor, Malaysia) ,  Othman Mohd Hafiz Dzarfan (Advanced Membrane Technology Research Centre (AMTEC), School of Chemical and Energy Engineering, Faculty of Engineering, Universiti Teknologi Malaysia, 81310, Skudai, Johor, Malaysia) ,  Jilani Asim (Advanced Membrane Technology Research Centre (AMTEC), School of Chemical and Energy Engineering, Faculty of Engineering, Universiti Teknologi Malaysia, 81310, Skudai, Johor, Malaysia) ,  Jilani Asim (Center of Nanotechnology, King Abdul-Aziz University, 21589, Jeddah, Saudi Arabia) ,  Ismail A.F. (Advanced Membrane Technology Research Centre (AMTEC), School of Chemical and Energy Engineering, Faculty of Engineering, Universiti Teknologi Malaysia, 81310, Skudai, Johor, Malaysia) ,  Hashim Haslenda (Process System Engineering Centre (PROSPECT), School of Chemical and Energy Engineering, Faculty of Engineering, Universiti Teknologi Malaysia, 81310, Skudai, Johor, Malaysia) ,  Jaafar Juhana (Advanced Membrane Technology Research Centre (AMTEC), School of Chemical and Energy Engineering, Faculty of Engineering, Universiti Teknologi Malaysia, 81310, Skudai, Johor, Malaysia) ,  Zulhairun A.K. (Advanced Membrane Technology Research Centre (AMTEC), School of Chemical and Energy Engineering, Faculty of Engineering, Universiti Teknologi Malaysia, 81310, Skudai, Johor, Malaysia) ,  Rahman Mukhlis A. (Advanced Membrane Technology Research Centre (AMTEC), School of Chemical and Energy Engineering, Faculty of Engineering, Universiti Teknologi Malaysia, 81310, Skudai, Johor, Malaysia) ,  Rehman Ghani Ur (Advanced Membrane Technology Research Centre (AMTEC), School of Chemical and Energy Engineering, Faculty of Engineering, Universiti Teknologi Malaysia, 81310, Skudai, Johor, Malaysia) ,  Khan Imran Ullah (Department of Chemical and Energy Engineering, Pak-Austria Fachhochshule, Institute of Applied Sciences&Technology, Khanpur Road, Mang, Haripur 22650, Pakistan)
資料名： Polymer Testing  (Polymer Testing)
巻： 84  ページ： Null  発行年： 2020年 
JST資料番号： C0752B  ISSN： 0142-9418  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 混合マトリックス膜(MMMs)は,透過性と選択性に関して,それらの優れた性能により天然ガス精製に世界的に注目されている。ゼオライトイミダゾールフレーム-8(ZIF-8)混合ポリスルホン(PSf)膜を天然ガス精製用に作製した。ZIF-8は,その低コスト,顕著な熱的および化学的安定性,および調整可能なミクロ多孔性構造のために選択された。1.25%までの種々のZIF-8負荷を組み込んだ純粋なPSf中空繊維膜と混合マトリックス中空繊維膜を作製した。調製した膜を,電界放出走査電子顕微鏡(FESEM),熱重量分析(TGA),示差走査熱量測定(DSC),Fourier変換赤外分光法(FTIR),原子間力顕微鏡(AFM),およびガス分離性能を用いて評価した。MMMへのZIF-8ナノ粒子の低負荷は,熱安定性とガラス転移温度を改善し,低い表面粗さをもたらした。MMMsは純ガスを用いて試験し,CO2透過率は36%,CO2/CH4選択性は28%であった。しかし,高いZIF-8負荷は分離性能を低下させた。さらに,CO_2/CH_4選択性は,CO_2誘導可塑化により,高圧(8および10bar)で減少した。以前に,ZIF-8粒子の組込みは主に平坦なシート膜の作製を受けてきたが,本研究はほとんど研究されていない中空繊維膜に焦点を当てた。したがって,本研究において低供給圧力で得られた有望な結果は,天然ガス精製のためのZIF-8ベース中空繊維膜の可能性を示した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 高圧 ,  *天然ガス ,  ガラス転移点 ,  熱重量分析 ,  二酸化炭素 ,  可塑化 ,  透過率 ,  示差走査熱量測定 ,  原子間力顕微鏡 ,  FTIR分光法 ,  ナノ粒子
準シソーラス用語： 分離性能 ,  電界放出型走査電子顕微鏡 ,  *ガス精製 ,  *ZIF-8 , 【Automatic Indexing@JST】

著者キーワード (4件)： 混合マトリックス膜 ,  ZIF-8 ,  ガス分離 ,  可塑化

分類 (5件)： 繊維材料一般  (YM01070O) ,  液体クロマトグラフィー  (CC04014L) ,  高分子材料一般  (YH07010B) ,  医用素材  (GA05040H) ,  抵抗性  (YH02050K)

タイトルに関連する用語 (3件)： ガス精製 ,  ZIF-8 ,  ポリスルホン中空糸膜