ポリウレタンマトリックス内にポリピロールで被覆したNi_0.25Co_0.25Ti_0.5Fe_2O_4/SrCoTiFe_10O_19/Cu複合材料の低負荷比の顕著なマイクロ波吸収効率【JST・京大機械翻訳】

Remarkable microwave absorption efficiency of low loading ratio of Ni_0.25Co_0.25Ti_0.5Fe₂O₄/SrCoTiFe₁₀O₁₉/Cu composite coated with polyprrole within polyurethane matrix

著者 (5件)： Xu Dong (College of Geomatics and Municipal Engineering, Zhejiang University of Water Resources and Electric Power, Hangzhou 310018, People’s Republic of China) ,  Jafarian Mojtaba (Department of Mechanical Engineering, Faculty of Engineering, Tehran North Branch, Islamic Azad University, Tehran, Iran) ,  Seyyed Afghahi Seyyed Salman (Department of Materials Science and Engineering, Imam Hossein University, Tehran, Iran) ,  Atassi Yomen (Department of Applied Physics, Higher Institute for Applied Sciences and Technology, Damascus, Syria) ,  Bani Al-Marjeh Rama Al-Qassar (Department of Applied Physics, Higher Institute for Applied Sciences and Technology, Damascus, Syria)
資料名： Materials Research Express  (Materials Research Express)
巻： 7  号： 1  ページ： 016103 (10pp)  発行年： 2020年 
JST資料番号： W5570A  ISSN： 2053-1591  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： NiCoTiスピネルフェライト,SrCoTi六方晶フェライトおよび銅微粒子を,その場化学酸化法を用いてポリピロール(PPY)で被覆した。得られたマイクロ波吸収材料をポリウレタンマトリックスに導入した。XRDパターンはスピネルと六方晶フェライトの成功した調製を示した。SEM顕微鏡写真は,調製した複合材料の半球状形態を示した。磁気特性をVSMを用いて調べた。20%w/w負荷率のマイクロ波吸収体は,最良のマイクロ波吸収性能(3GHzの-10dB以下の帯域幅と整合周波数9.75GHzでの-24dBの反射損失と1.8mmの厚さ)を示した。誘電率と透磁率の測定は,誘電損失機構が電流吸収体において支配的であることを明らかにした。自由空間法を用いて測定した反射損失も,20%w/wの負荷率を有する試料の優れた性能を示した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 六方晶系 ,  *ポリピロール ,  誘電損失 ,  スピネル ,  帯域幅 ,  酸化 ,  透磁率 ,  微粒子 ,  電流 ,  フェライト ,  誘電率 ,  X線回折 ,  *ポリウレタン ,  銅 ,  吸収体

分類 (2件)： 電磁気学一般  (BD01020N) ,  セラミック・磁器の性質  (YC03030G)

タイトルに関連する用語 (7件)： ポリウレタン ,  マトリックス ,  ポリピロール ,  Cu ,  複合材料 ,  マイクロ波 ,  吸収効率