溶融塩媒介の還元により調製したTiB_2六角板の成長挙動【JST・京大機械翻訳】

Growth behavior of TiB₂ hexagonal plates prepared via a molten-salt-mediated carbothermal reduction

著者 (8件)： Song Shaolei (Research Center of Nano Science and Technology, Shanghai University, Shanghai, China) ,  Song Shaolei (School of Materials Science and Engineering, Shanghai University, Shanghai, China) ,  Zhang Tong (Research Center of Nano Science and Technology, Shanghai University, Shanghai, China) ,  Xie Chen (School of Materials Science and Engineering, Shanghai University, Shanghai, China) ,  Zhou Jianmin (Research Center of Nano Science and Technology, Shanghai University, Shanghai, China) ,  Li Rong (Research Center of Nano Science and Technology, Shanghai University, Shanghai, China) ,  Zhen Qiang (Research Center of Nano Science and Technology, Shanghai University, Shanghai, China) ,  Zhen Qiang (School of Materials Science and Engineering, Shanghai University, Shanghai, China)
資料名： Journal of the American Ceramic Society  (Journal of the American Ceramic Society)
巻： 103  号： 2  ページ： 719-723  発行年： 2020年 
JST資料番号： C0253A  ISSN： 0002-7820  CODEN： JACTAW  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： TiB_2粉末を,溶融塩媒介炭素熱還元法によって首尾よく合成した。1300°C,2時間で得られた生成物は,3~8μmの辺長と200~500nmの厚さの六方晶系板であった。温度による微細構造の発達は,TiB_2六方晶板の成長が二次元核形成によって制御された層毎の成長であることを確認した。不均一な結晶粒がTiB_2板の側面とステップ端に付着して観察され,それは微細になり,成長の間に消失した。これは,TiB_2板の側面上の層成長と成長が表面吸着成長モデルに従うことを示した。Copyright 2020 Wiley Publishing Japan K.K. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 粉体 ,  二次元 ,  核形成 ,  微細構造 ,  結晶成長 ,  結晶粒 ,  *融解塩 ,  六方晶系
準シソーラス用語： 成長モデル ,  表面吸着 ,  炭素熱還元 , 【Automatic Indexing@JST】

著者キーワード (4件)： 粒成長 ,  溶融塩合成 ,  プレート ,  二ほう化チタン

分類 (4件)： セラミック・磁器の性質  (YC03030G) ,  非金属材料へのセラミック被覆  (YC02040K) ,  セラミック・陶磁器の製造  (YC03020V) ,  塩基,金属酸化物  (CD01030Z)

タイトルに関連する用語 (5件)： 溶融塩 ,  還元 ,  調製 ,  成長 ,  挙動