高分子マトリックスのグループまたはセグメントによるCOF表面修飾によるCO_2/H_2分離のための高性能および耐圧性混合マトリックス膜の調製【JST・京大機械翻訳】

Preparation of high-performance and pressure-resistant mixed matrix membranes for CO₂/H₂ separation by modifying COF surfaces with the groups or segments of the polymer matrix

著者 (17件)： Cao Xiaochang (Chemical Engineering Research Center, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Cao Xiaochang (Tianjin Key Laboratory of Membrane Science and Desalination Technology, State Key Laboratory of Chemical Engineering, Collaborative Innovation Center of Chemical Science and Engineering, Tianjin University, Tianjin, 300350, PR China) ,  Cao Xiaochang (School of Environmental and Municipal Engineering, Tianjin Chengjian University, Tianjin, 300387, PR China) ,  Xu Haoqing (Chemical Engineering Research Center, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Xu Haoqing (Tianjin Key Laboratory of Membrane Science and Desalination Technology, State Key Laboratory of Chemical Engineering, Collaborative Innovation Center of Chemical Science and Engineering, Tianjin University, Tianjin, 300350, PR China) ,  Dong Songlin (Chemical Engineering Research Center, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Dong Songlin (Tianjin Key Laboratory of Membrane Science and Desalination Technology, State Key Laboratory of Chemical Engineering, Collaborative Innovation Center of Chemical Science and Engineering, Tianjin University, Tianjin, 300350, PR China) ,  Xu Jiayou (Chemical Engineering Research Center, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Xu Jiayou (Tianjin Key Laboratory of Membrane Science and Desalination Technology, State Key Laboratory of Chemical Engineering, Collaborative Innovation Center of Chemical Science and Engineering, Tianjin University, Tianjin, 300350, PR China) ,  Qiao Zhihua (Chemical Engineering Research Center, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Qiao Zhihua (Tianjin Key Laboratory of Membrane Science and Desalination Technology, State Key Laboratory of Chemical Engineering, Collaborative Innovation Center of Chemical Science and Engineering, Tianjin University, Tianjin, 300350, PR China) ,  Zhao Song (Chemical Engineering Research Center, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Zhao Song (Tianjin Key Laboratory of Membrane Science and Desalination Technology, State Key Laboratory of Chemical Engineering, Collaborative Innovation Center of Chemical Science and Engineering, Tianjin University, Tianjin, 300350, PR China) ,  Wang Jixiao (Chemical Engineering Research Center, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Wang Jixiao (Tianjin Key Laboratory of Membrane Science and Desalination Technology, State Key Laboratory of Chemical Engineering, Collaborative Innovation Center of Chemical Science and Engineering, Tianjin University, Tianjin, 300350, PR China) ,  Wang Zhi (Chemical Engineering Research Center, School of Chemical Engineering and Technology, Tianjin University, Tianjin, 300350, PR China) ,  Wang Zhi (Tianjin Key Laboratory of Membrane Science and Desalination Technology, State Key Laboratory of Chemical Engineering, Collaborative Innovation Center of Chemical Science and Engineering, Tianjin University, Tianjin, 300350, PR China)
資料名： Journal of Membrane Science  (Journal of Membrane Science)
巻： 601  ページ： Null  発行年： 2020年 
JST資料番号： E0669A  ISSN： 0376-7388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,CO_2/H_2分離のための高性能で耐圧性の混合マトリックス膜(MMMs)を調製する簡単な方法を提案した。ポリ-(ビニルアミン)(PVAm)のグループまたはセグメントを用いて共有結合有機骨格(COF)を修飾し,類似の骨格を持つが異なる表面を得た。次に,改質COFをPVAmマトリックスと混合し,改質ポリスルホン(MPSF)を被覆して,CO_2/H_2分離のためのMMMsを調製した。改質COFおよびPVAmマトリックスは,COF表面がPVAmと同じグループまたはセグメントを有するため,非常に適合性があった。一方,被覆溶液において,COF表面は,COF細孔へのPVAm分子の浸透を誘導し,COFの細孔サイズを狭くし,CO_2優先吸収と輸送のためのアミノ環境を提供することが分かった。浸透度はCOF表面とPVAm分子間の水素結合により影響を受けた。さらに,組み込まれたCOFはPVAmマトリックスの移動度を効果的に制限し,高圧下でMMMsに対する圧力抵抗を増加させた。ガス透過試験において,最適MMMsは,チャネル(0.94nm)の高い適合性とサイズのために,2.0MPaにおいて,957GPUのCO_2透過率と17.1のCO_2/H_2選択性を達成することができた。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 界面 ,  適応性 ,  二酸化炭素 ,  水素結合 ,  表面改質 ,  細孔 ,  細孔径 ,  耐圧性 ,  透過率 ,  *被覆 ,  移動度 ,  チャネル ,  高圧 ,  共有結合
準シソーラス用語： 気体透過 , 【Automatic Indexing@JST】

著者キーワード (6件)： 共有結合有機骨格 ,  CO2/H2分離 ,  浸透度 ,  CO2優先吸収チャンネル ,  圧力抵抗 ,  界面適合性

分類 (2件)： 膜分離  (XD02120Z) ,  その他の高分子材料  (YH07150C)

タイトルに関連する用語 (9件)： 高分子マトリックス ,  グループ ,  セグメント ,  COF ,  表面修飾 ,  高性能 ,  耐圧性 ,  混合マトリックス膜 ,  調製