導電性Al-Y-Sc合金の構造及び性質に及ぼすYbの影響【JST・京大機械翻訳】

Effect of Yb on the Structure and Properties of an Electroconductive Al-Y-Sc Alloy

著者 (8件)： Barkov R. Yu. (National University of Science and Technology MISiS, Moscow, Russia) ,  Yakovtseva O. A. (National University of Science and Technology MISiS, Moscow, Russia) ,  Mamzurina O. I. (National University of Science and Technology MISiS, Moscow, Russia) ,  Loginova I. S. (National University of Science and Technology MISiS, Moscow, Russia) ,  Medvedeva S. V. (National University of Science and Technology MISiS, Moscow, Russia) ,  Proviryakov A. S. (National University of Science and Technology MISiS, Moscow, Russia) ,  Mikhaylovskaya A. V. (National University of Science and Technology MISiS, Moscow, Russia) ,  Pozdniakov A. V. (National University of Science and Technology MISiS, Moscow, Russia)
資料名： Physics of Metals and Metallography  (Physics of Metals and Metallography)
巻： 121  号： 6  ページ： 604-609  発行年： 2020年 
JST資料番号： W1091A  ISSN： 0031-918X  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本研究では,Al-0.2%Y-0.2Sc合金の圧延前後の焼鈍による相組成,強化,および電気伝導率と機械的性質に及ぼすイッテルビウム添加の影響を調べた。サイズが100~250nmの金属間化合物相の粒子がイットリウムとイッテルビウムに富んでいる分散共晶をアルミニウム固溶体とは別に鋳造構造で明らかにした。インゴットの最大強化は,Al_3M分散体の析出により300°Cで3時間焼鈍後に達成された。300°Cでの変形シートのアニーリングは,アルミニウム固溶体の付加的分解のプロセスの開始と結びついた硬度および降伏強度の増加をもたらした。これは,イッテルビウムの添加が,圧延後焼鈍プロセスにおけるAl_3M分散体の不均一核形成を刺激することを意味する。この場合,アニールした銅の国際標準に従って,電気伝導率は,200°Cと300°Cでアニール後,それぞれ54から54.9%と57.7%までアニーリングの温度と時間の増加と共に増加する。Copyright Pleiades Publishing, Ltd. 2020 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 共晶 ,  金属間化合物 ,  固溶体 ,  焼なまし ,  電気伝導率 ,  *アルミニウム ,  *イッテルビウム ,  イットリウム ,  銅 ,  鋳造 ,  圧延 ,  インゴット ,  国際規格 ,  降伏強さ ,  *導電性

著者キーワード (6件)： アルミニウム合金 ,  イットリウム ,  イッテルビウム ,  微細構造 ,  機械的性質 ,  電気伝導率

分類 (2件)： 変態組織,加工組織  (WB01030N) ,  機械的性質  (WB02030U)

タイトルに関連する用語 (5件)： 導電性 ,  Al ,  Sc合金 ,  性質 ,  Yb