ヒト剥離乳歯培養から幹細胞を培養するための表面官能化エレクトロスピニングポリカプロラクトン繊維【JST・京大機械翻訳】

Surface-functionalized Electrospun Polycaprolactone Fiber for Culturing Stem Cell from Human Exfoliated Deciduous Teeth Culture

著者 (5件)： Jitpibull Jirasak (School of Materials Science and Innovation, Faculty of Science, Mahidol University, Nakhon Pathom, Thailand) ,  Vongsetskul Thammasit (School of Materials Science and Innovation, Faculty of Science, Mahidol University, Nakhon Pathom, Thailand) ,  Vongsetskul Thammasit (Department of Chemistry, Faculty of Science, Mahidol University, Bangkok, Thailand) ,  Sritanaudomchai Hathaitip (Department of Oral Biology, Faculty of Dentistry, Mahidol University, Bangkok, Thailand) ,  Tangjit Nathaphon (Department of Orthodontics, Faculty of Dentistry, Mahidol University, Bangkok, Thailand)
資料名： Fibers and Polymers  (Fibers and Polymers)
巻： 21  号： 10  ページ： 2215-2223  発行年： 2020年 
JST資料番号： W4363A  ISSN： 1229-9197  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 2.8ミクロンの平均直径と25ミクロンの細孔径を有する平滑でビーズフリーのポリカプロラクトン(PCL)繊維を,クロロホルム:メチルアルコール混合物(体積で3:1)に溶解した17wt%w/wPCLから20kV,繊維収集距離15cm,ノズル直径0.9mm,および5時間2ml/hで紡糸した。次に,繊維表面をゼラチン(GE)によって固定化し,ヒアルロン酸(HA)によって被覆し,GE-PCL,HA-PCL,およびHA-GE-PCLをそれぞれ得るために,両方のプロセスで実施した。処理した繊維は水によって完全に濡れたが,PCL繊維はそうではなかった。GEは熱安定性を改善したが,HAは繊維の引張強さと弾性率を増加させた。GEとHAの両方が破断時の伸びを減少させた。ヒト落葉歯(SHED)からの幹細胞を選択し,繊維上の増殖を調べた:GE-PCL>HA-PCL gt;PCL。Copyright The Korean Fiber Society 2020 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 弾性係数 ,  破断 ,  ゼラチン ,  ヒト ,  紡糸 ,  落葉 ,  引張強さ ,  粒状材 ,  *乳歯 ,  細孔径 ,  *ポリカプロラクトン ,  *幹細胞 ,  生体組織工学
準シソーラス用語： 固定化 ,  *表面官能化 , 【Automatic Indexing@JST】

著者キーワード (5件)： 繊維 ,  ゼラチン ,  ヒト剥離乳歯 ,  ポリカプロラクトン ,  組織工学

分類 (2件)： 医用素材  (GA05040H) ,  その他の紡糸・製糸  (YM03050G)

タイトルに関連する用語 (6件)： ヒト ,  乳歯 ,  培養 ,  幹細胞 ,  表面官能化 ,  繊維