文献

J-GLOBAL ID：202002291442417146   整理番号：20A0064100

空気中で調製したCe3+ドープアルミノホウケイ酸塩ガラスの発光強度の増強【JST・京大機械翻訳】

Enhanced emission intensity of Ce³⁺-doped aluminoborosilicate glasses prepared in air

著者 (7件)： Sun Xin-Yuan (Department of Physics, Jinggangshan University, Ji’an, 343009, PR China) ,  Liu Xiu-Jian (Department of Physics, Jinggangshan University, Ji’an, 343009, PR China) ,  Wu Yuntao (R&D Center of Synthetic Crystal, Shanghai Institute of Ceramics, Chinese Academy of Sciences, Jiading, 201899, PR China) ,  Xiao Zhuohao (Materials Science and Engineering, Jingdezhen Ceramic Institute, Jingdezhen, 333001, PR China) ,  Chen Quan (Department of Physics, Jinggangshan University, Ji’an, 343009, PR China) ,  Wang Wen-Feng (Department of Physics, Jinggangshan University, Ji’an, 343009, PR China) ,  Yang Qing-Mei (Library of Jinggangshan University, Ji’an, 343009, PR China)
資料名： Ceramics International  (Ceramics International)
巻： 46  号： 3  ページ： 4035-4038  発行年： 2020年 
JST資料番号： H0705A  ISSN： 0272-8842  資料種別： 逐次刊行物 (A)
記事区分： 短報  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高温溶融急冷法により空気中で無色で透明なCe3+ドープアルミノけい酸塩ガラスを調製する便利で効果的な戦略を明らかにした。それは,SiO_2に対するSi_3N_4の部分置換により,20~25mol%の範囲で容易に達成された。最適化されたCe3+をドープしたアルミノホウ酸塩ガラス(y=25%)は,それぞれ4.6432g/cm3の密度と35.36nsの寿命を示した。Si_3N_4(y=0%)の置換のないガラスと比較して,最適化したCe3+ドープアルミノホウ酸塩ガラス(y=25%)の光および放射ルミネセンス強度の両方は,それぞれ11.05および10.58の因子によって強化された。対応する積分レードルミネセンス強度はX線で照射したBGO結晶の約22.8%であった。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 放射線ルミネセンス ,  *ドーピング ,  結晶 ,  *ガラス ,  急冷 ,  アルミノケイ酸ガラス ,  窒化ケイ素 ,  無色 ,  最適化 ,  *ホウケイ酸ガラス ,  光ルミネセンス ,  ホウ酸塩ガラス ,  ルミネセンス ,  高温
準シソーラス用語： *セリウムイオン , 【Automatic Indexing@JST】

著者キーワード (4件)： Ce3+ドープアルミノホウケイ酸塩ガラス ,  窒化ケイ素 ,  光ルミネセンス ,  放射線ルミネセンス

分類 (1件)： 無機化合物のルミネセンス  (BM08093J)

タイトルに関連する用語 (8件)： 空気中 ,  調製 ,  Ce3+ ,  ドープ ,  アルミ ,  ホウケイ酸塩ガラス ,  発光強度 ,  増強