6061Al合金のAC TIG突合せ溶接継手の微細組織および特性に及ぼすHFパルス効果【JST・京大機械翻訳】

HF pulse effect on microstructure and properties of AC TIG butt-welded joint of 6061Al alloy

著者 (4件)： Wang Yajie (MOE Key Laboratory for Liquid-Solid Structure Evolution and Materials Processing, Institute for Materials Joining, Shandong University, Jinan, 250061, PR China) ,  Wang Yajie (Shanghai Key Laboratory of Materials Laser Processing and Modification, School of Materials Science and Engineering, Shanghai Jiao Tong University, Shanghai, 200240, PR China) ,  Chen Maoai (MOE Key Laboratory for Liquid-Solid Structure Evolution and Materials Processing, Institute for Materials Joining, Shandong University, Jinan, 250061, PR China) ,  Wu Chuansong (MOE Key Laboratory for Liquid-Solid Structure Evolution and Materials Processing, Institute for Materials Joining, Shandong University, Jinan, 250061, PR China)
資料名： Journal of Manufacturing Processes  (Journal of Manufacturing Processes)
巻： 56  号： PA  ページ： 878-886  発行年： 2020年 
JST資料番号： W3312A  ISSN： 1526-6125  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 6061アルミニウム合金の6mm厚さの突合せ継手溶接を用いて,フィラーワイヤ添加による高周波(HF)パルス変調方形波AC TIG(HFPM AC TIG)溶接を特性化した。完全に浸透した溶接を達成するために必要な熱入力は,変調HFパルスによって著しく減少する。同じ等価電流で,溶接侵入は増加し,溶接幅は減少する。部分溶融ゾーン,溶解ゾーンおよび過時効ゾーンの幅は,すべて減少した。溶融線周りの柱状結晶粒の形成が抑制され,等軸粒の形成が促進された。溶接金属におけるミクロ孔の数密度と平均サイズは,大いに減少した。溶接熱サイクルの軟化効果は大幅に緩和された。溶接継手の強度と伸びは,それぞれ,8.5%と19.8%増加し,溶接金属の強度と伸びは,それぞれ,6.1%と46.1%増加した。Copyright 2020 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 電流 ,  溶解 ,  アルミニウム合金 ,  *溶接 ,  *突合せ溶接継手 ,  *溶接継手 ,  パルス変調 ,  部分融解 ,  矩形波 ,  引張強さ ,  *パルス ,  溶接金属 ,  柱状晶 ,  過時効
準シソーラス用語： 突合せ継手 , 【Automatic Indexing@JST】

著者キーワード (3件)： HFPM AC TIG ,  微細構造 ,  引張強度

分類 (2件)： 機械的性質  (WB02030U) ,  溶接部  (WC07100I)

タイトルに関連する用語 (5件)： Ac ,  突合せ溶接継手 ,  微細組織 ,  HF ,  パルス