Ta/Cu多層によるTC4からIN718へのバイメタル構造のレーザ付加製造【JST・京大機械翻訳】

Laser additive manufacturing of bimetallic structure from TC4 to IN718 via Ta/Cu multi-interlayer

著者 (5件)： Wang Chenyang (School of Material Science and Engineering, Shenyang University of Technology, Shenyang 110870, People’s Republic of China) ,  Shang Chun (School of Material Science and Engineering, Shenyang University of Technology, Shenyang 110870, People’s Republic of China) ,  Liu Zhanqi (School of Material Science and Engineering, Shenyang University of Technology, Shenyang 110870, People’s Republic of China) ,  Xu Guojian (School of Material Science and Engineering, Shenyang University of Technology, Shenyang 110870, People’s Republic of China) ,  Liu Xiangyu (R & D department, Liaoning additive manufacturing industry technology Research Institute Co., Ltd., Shenyang 110206, People’s Republic of China)
資料名： Materials Research Express  (Materials Research Express)
巻： 7  号： 12  ページ： 126506 (8pp)  発行年： 2020年 
JST資料番号： W5570A  ISSN： 2053-1591  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： チタン合金とニッケル基合金は,それら自身のユニークな性質を有し,2つの合金から成る二金属構造は,航空宇宙分野で広く使用できる。しかし,チタン合金とニッケル基合金を従来の方法で直接接合して作製した二金属構造は金属間化合物の形成により亀裂に敏感である。本研究では,レーザ付加製造(LAM)技術に基づき,Ta/Cu多層により,冶金欠陥の無いTC4/IN718バイメタル構造(亀裂のような)を成功裏に作製した。試験結果は,Ta/Cuマルチ中間層がTC4とIN718の間のTi-NiとTi-Cu金属間化合物の生成を効果的に避けることができることを示した。冶金的欠陥のないTC4からIN718までの各界面に良好な冶金的組合せが形成された。TC4領域からIN718領域への相変化は次の通りであった。α-Ti→α-Ti+β-Ta→β-Ta+γ-Cu→γ-Cu+γ-Ni+laves→γ-Ni+laves。室温での二金属構造の極限引張強度は369.32MPaであった。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 亀裂 ,  金属間化合物 ,  合金 ,  相転移 ,  *タンタル ,  *銅 ,  チタン合金 ,  ニッケル合金 ,  バイメタル ,  金属構造 ,  引張強さ ,  冶金 ,  多層 ,  *付加製造
準シソーラス用語： 中間層 , 【Automatic Indexing@JST】

分類 (4件)： 機械的性質  (WB02030U) ,  鋳造法,鋳込  (WC01030Q) ,  溶接部  (WC07100I) ,  クラッド材  (WE04020G)

タイトルに関連する用語 (8件)： Ta ,  Cu ,  多層 ,  TC4 ,  IN718 ,  バイメタル ,  レーザ ,  付加製造