Zr-Cu-Fe-Al系におけるバルク金属ガラス形成組成を予測するための熱力学モデルとDy添加の役割の理解【JST・京大機械翻訳】

Thermodynamic model to predict bulk metallic glass forming composition in Zr-Cu-Fe-Al system and understanding the role of Dy addition

著者 (5件)： Prabhu Yogesh (Department of Metallurgical &Materials Engineering, Visvesvaraya National Institute of Technology, Nagpur, 440010, India) ,  Srivastav Ajeet K. (Department of Metallurgical &Materials Engineering, Visvesvaraya National Institute of Technology, Nagpur, 440010, India) ,  Gunderov D.V. (Ufa State Aviation Technical University, 12 K. Marx str., Ufa, 450008, Russia) ,  Gunderov D.V. (Institute of Molecule and Crystal Physics UFRC RAS, 71 pr. Oktyabrya, Ufa, 450054, Russia) ,  Bhatt Jatin (Department of Metallurgical &Materials Engineering, Visvesvaraya National Institute of Technology, Nagpur, 440010, India)
資料名： Physica B. Condensed Matter  (Physica B. Condensed Matter)
巻： 624  ページ： Null  発行年： 2022年 
JST資料番号： H0676B  ISSN： 0921-4526  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,熱力学的枠組みの下で,NiフリーZr-Cu-Al-Fe四元系中のZrリッチガラス形成組成を設計する理論的アプローチを提案した。本研究では,構成エントロピーの統計フレームワーク(ΔS構成/R)における化学的混合(ΔHchem)と原子サイズミスマッチエントロピー(ΔSσ/kB)のエンタルピーを決定するために,構成元素間の化学的相互作用とトポロジー的特徴を最適化することにより,四元組成を設計した。さらに,ガラス形成能力(GFA)に及ぼすZr-Cu系中の元素AlとFe添加の影響を熱力学的観点から解析した。また,Zr-Cu-Al-Fe系の熱力学とGFAに及ぼすDy添加の影響を理解するために試みを行った。その後,Zr_62Cu_22Al_10Fe_5Dy_1バルク金属ガラスを更なる研究のために合成した。Copyright 2021 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 位相幾何学 ,  エンタルピー ,  エントロピー ,  最適化 ,  *熱力学 ,  *アルミニウム ,  *ジスプロシウム ,  *鉄 ,  *熱力学模型 ,  *ガラス成形 ,  *バルク金属ガラス
準シソーラス用語： 四成分系 ,  ガラス形成能 ,  ニッケルフリー ,  化学的相互作用 , 【Automatic Indexing@JST】

著者キーワード (4件)： バルク金属ガラス ,  熱力学モデリング ,  四成分系 ,  希土類金属

分類 (2件)： ガラスの性質・分析・試験  (YC02030Z) ,  無機化合物のルミネセンス  (BM08093J)

タイトルに関連する用語 (11件)： Zr ,  Cu ,  Fe ,  Al ,  バルク金属ガラス ,  組成 ,  予測 ,  熱力学モデル ,  Dy ,  役割 ,  理解