ナノ濾過のためのポリドーパミン修飾ZIF-8を含むポリアミド薄膜ナノ複合材料膜【JST・京大機械翻訳】

Polyamide thin film nanocomposite membrane containing polydopamine modified ZIF-8 for nanofiltration

著者 (16件)： Zhao Bin (State Key Laboratory of Separation Membranes and Membrane Processes / National Center for International Joint Research on Separation Membranes, Tiangong University, Tianjin, 300387, China) ,  Zhao Bin (School of Environmental Science and Engineering, Tiangong University, Tianjin, 300387, China) ,  Long Xingli (School of Environmental Science and Engineering, Tiangong University, Tianjin, 300387, China) ,  Wang Hongli (School of Environmental Science and Engineering, Tiangong University, Tianjin, 300387, China) ,  Wang Liang (State Key Laboratory of Separation Membranes and Membrane Processes / National Center for International Joint Research on Separation Membranes, Tiangong University, Tianjin, 300387, China) ,  Qian Yiran (School of Environmental Science and Engineering, Tiangong University, Tianjin, 300387, China) ,  Zhang Hongwei (State Key Laboratory of Separation Membranes and Membrane Processes / National Center for International Joint Research on Separation Membranes, Tiangong University, Tianjin, 300387, China) ,  Zhang Hongwei (School of Environmental Science and Engineering, Tiangong University, Tianjin, 300387, China) ,  Yang Chenyang (School of Environmental Science and Engineering, Tiangong University, Tianjin, 300387, China) ,  Zhang Zhaohui (State Key Laboratory of Separation Membranes and Membrane Processes / National Center for International Joint Research on Separation Membranes, Tiangong University, Tianjin, 300387, China) ,  Zhang Zhaohui (School of Environmental Science and Engineering, Tiangong University, Tianjin, 300387, China) ,  Li Junjing (State Key Laboratory of Separation Membranes and Membrane Processes / National Center for International Joint Research on Separation Membranes, Tiangong University, Tianjin, 300387, China) ,  Li Junjing (School of Environmental Science and Engineering, Tiangong University, Tianjin, 300387, China) ,  Ma Cong (State Key Laboratory of Separation Membranes and Membrane Processes / National Center for International Joint Research on Separation Membranes, Tiangong University, Tianjin, 300387, China) ,  Ma Cong (School of Environmental Science and Engineering, Tiangong University, Tianjin, 300387, China) ,  Shi Yawei (State Key Laboratory of Separation Membranes and Membrane Processes / National Center for International Joint Research on Separation Membranes, Tiangong University, Tianjin, 300387, China)
資料名： Colloids and Surfaces. A. Physicochemical and Engineering Aspects  (Colloids and Surfaces. A. Physicochemical and Engineering Aspects)
巻： 612  ページ： Null  発行年： 2021年 
JST資料番号： A0539B  ISSN： 0927-7757  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 薄膜ナノ複合材料(TFN)膜作製のための水溶液中でゼオライトイミダゾラート骨格-8(ZIF-8)をより良く分散するために,親水性ZIF-8をポリドーパミン修飾によって調製した。界面重合(IP)反応後,PDA-ZIF-8ナノ粒子をポリアミド(PA)マトリックス中に均一に捕捉した。得られたPA層は,より良い親水性,より高い表面粗さ,およびより少ない架橋度を示した。したがって,水透過性はナノ充填剤のない薄膜複合材料(TFC)膜と比較して66%増加した。さらに,PDA-ZIF-8の相溶性の改善と,より強い負電荷膜表面により,SO_42-の保持はわずかに増強され,ローダミンBの保持は良く維持された。PDAによるZIF-8の親水性修飾は,PAポリマーとの相溶性を改善する容易な方法であり,得られたTFN膜は,その選択性を損なうことなく,高い水透過性を示した。Copyright 2021 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 重合体 ,  *薄膜 ,  *ポリアミド ,  親水性 ,  相溶性 ,  界面重合 ,  架橋度 ,  負電荷 ,  ナノ複合材料 ,  ナノ濾過 ,  ナノ粒子 ,  芳香族アミン ,  芳香族カルボン酸 ,  酸素複素環化合物 ,  キノイド化合物 ,  インモニウム ,  芳香族縮合化合物 ,  第三アミン
準シソーラス用語： ナノフィラー ,  *ポリドーパミン ,  *ZIF-8 , 【Automatic Indexing@JST】

著者キーワード (5件)： 薄膜ナノ複合材料膜 ,  ZIF-8 ,  ポリドーパミン ,  親水性修飾 ,  ナノろ過