NiCr-Alデトネーション被覆の構造,硬度及び耐摩耗性【JST・京大機械翻訳】

Structure, Hardness and Wear Resistance of the NiCr-Al Detonation Coating

著者 (6件)： Meruyert Maulet (Sarsen Amanzholov East Kazakhstan University,Scientific research center 《Surface engineering and tribology》,Ust-Kamenogorsk,Kazakhstan) ,  Rakhadilov Bauyrzhan (Sarsen Amanzholov East Kazakhstan University,Scientific research center 《Surface engineering and tribology》,Ust-Kamenogorsk,Kazakhstan) ,  Stepanova Olga (Shakarim University,Faculty of engineering and technological,Semei,Kazakhstan) ,  Sagdoldina Zhuldyz (Sarsen Amanzholov East Kazakhstan University,Scientific research center 《Surface engineering and tribology》,Ust-Kamenogorsk,Kazakhstan) ,  Kassymov Askar (Shakarim University,Faculty of engineering and technological,Semei,Kazakhstan) ,  Kakimzhanov Dauir (D. Serikbaev East Kazakhstan Technical University,Faculty of basic engineering training,Ust-Kamenogorsk,Kazakhstan)
資料名： IEEE Conference Proceedings  (IEEE Conference Proceedings)
巻： 2020  号： NAP  ページ： 01TFC17-1-01TFC17-3  発行年： 2020年 
JST資料番号： W2441A  資料種別： 会議録 (C)
記事区分： 原著論文  発行国： アメリカ合衆国 (USA)  言語： 英語 (EN)

抄録/ポイント： 本論文は,爆発性アセチレン-酸素混合物でデトネーションバレルを充填する体積の異なる値で得られたNi-Cr-Al耐摩耗性デトネーション被覆の特性を研究した。バレルが40%の爆発ガス混合物で満たされたとき,被覆は,個々の粒子の間の顕著な境界を持ち,十分に緻密でなく,それは,噴霧粉末の粒子の不十分な加熱と加速の結果である可能性がある。バレルの50%充填でより高い微小硬さ値が得られた。被覆のトライボロジー試験の結果から,爆発混合物によるデトネーションバレルを充填する体積が60%までは,他の被覆より低い摩耗率を有することがわかった。デトネーションバレル充填体積の50%での質量損失は他の被覆より少ない。Copyright 2021 The Institute of Electrical and Electronics Engineers, Inc. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 混合気体 ,  *耐摩耗性 ,  *デトネーション ,  微小硬さ ,  *被覆 ,  トライボロジー ,  硬度 ,  爆発性 ,  摩耗率
準シソーラス用語： アトマイズ金属粉末 ,  質量損失 , 【Automatic Indexing@JST】