純曲げにおける異方性溶接亀裂板に対する限界荷重解【JST・京大機械翻訳】

A Limit Load Solution for Anisotropic Welded Cracked Plates in Pure Bending

著者 (6件)： Alexandrov Sergei (Ishlinsky Institute for Problems in Mechanics RAS, 119526 Moscow, Russia) ,  Alexandrov Sergei (Federal State Autonomous Educational Institution of Higher Education, South Ural State University (National Research University), 454080 Chelyabinsk, Russia) ,  Lyamina Elena (Ishlinsky Institute for Problems in Mechanics RAS, 119526 Moscow, Russia) ,  Pirumov Alexander (Department of Elektrotechnics and Mechanics, Russian Technological University (MIREA), 119454 Moscow, Russia) ,  Nguyen Dinh Kien (Institute of Mechanics, VAST, 18 Hoang Quoc Viet, Hanoi 100000, Vietnam) ,  Nguyen Dinh Kien (Faculty of Mechanics and Automation, Graduate University of Science and Technology, VAST, 18 Hoang Quoc Viet, Hanoi 100000, Vietnam)
資料名： Symmetry (Web)  (Symmetry (Web))
巻： 12  号： 11  ページ： 1764  発行年： 2020年 
JST資料番号： U7282A  ISSN： 2073-8994  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： 本論文では,純曲げにおける溶接板に対する単純な上限解を導いた。板は,溶接に位置する亀裂を含む。溶接と母材の両方が直交異方性である。Hills二次降伏基準を採用した。解は半解析である。数値的方法は,2つの独立変数の関数を最小化するためにのみ必要である。6つの独立した無次元パラメータは構造を分類する。したがって,解の完全なパラメータ解析は実行可能ではない。しかし,与えられたパラメータセットに対して,数値解は簡単で,数値法は高速である。数値例は塑性崩壊における曲げモーメントに及ぼす塑性異方性と亀裂位置の影響を強調する。特に,対称の垂直軸を持つ試験片の曲げモーメントを非対称試験片と比較した。後者が全ての考慮事例で小さいことを示した。見出された解は,欠陥評価手順と共に使用できる。Copyright 2021 The Author(s) All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 異方性 ,  *亀裂 ,  数値解法 ,  対称性 ,  直交異方性 ,  曲げモーメント ,  *溶接 ,  *溶接割れ ,  降伏 ,  非対称性 ,  *終局荷重 ,  塑性異方性
準シソーラス用語： 独立変数 ,  パラメトリック解析 ,  無次元パラメータ , 【Automatic Indexing@JST】

著者キーワード (4件)： 溶接継手 ,  亀裂 ,  限界荷重 ,  異方性

分類 (3件)： 平板  (HD03060Z) ,  金属材料  (HC03020E) ,  溶接設計,溶接構造物  (WC07140A)

引用文献 (42件)：

• Varma, A.; Yadavalli, R.K. Failure analysis of a reheater tube dissimilar metal weld failure in a 500 MW power plant. Eng. Fail. Anal. 2020, 118, 104851.
• Xu, X.; Siefert, J.A.; Parker, J.D.; Thomson, R.C. Influence of microstructure on cavitation in the heat affected zone of a Grade 92 steel weld during long-term high temperature creep. Mater. Charact. 2020, 170, 110663.
• Han, Q.; Wang, X.; Lu, Y. Effect of corrosion on the fatigue behaviour of butt welds of G20Mn5QT cast steel and Q345D hot rolled steel in 3.5-wt% NaCl solution. Fatigue Fract. Eng. Mater. Struct. 2020, 43, 2703-2714.
• Mehmanparast, A.; Yatomi, M.; Biglari, F.; Maleki, S.; Nikbin, K. Experimental and numerical investigation of the weld geometry effects on Type IV cracking behaviour in P91 steel. Eng. Fail. Anal. 2020, 117, 104826.
• Peng, J.; Hou, C.; Shen, L. Numerical simulation of weld fracture using cohesive interface for novel inter-module connections. J. Constr. Steel Res. 2020, 174, 106302.

タイトルに関連する用語 (4件)： 異方性 ,  溶接亀裂 ,  限界荷重 ,  解