マグネシウムの生物分解と生体適合性に及ぼす低希土類元素(ランタン, ネオジム, セリウム)添加の影響【JST・京大機械翻訳】

Effect of the addition of low rare earth elements (lanthanum, neodymium, cerium) on the biodegradation and biocompatibility of magnesium

著者 (21件)： Willbold Elmar (Laboratory for Biomechanics and Biomaterials, Department of Orthopaedic Surgery, Hannover Medical School, Anna-von-Borries-Strasse 1-7, 30625 Hannover, Germany) ,  Willbold Elmar (CrossBIT, Center for Biocompatibility and Implant-Immunology, Department of Orthopaedic Surgery, Hannover Medical School, Feodor-Lynen-Strasse 31, 30625 Hannover, Germany) ,  Gu Xuenan (Department of Materials Science and Engineering, College of Engineering, Peking University, No. 5 Yi-He-Yuan Road, Hai-Dian District, Beijing 100871, China) ,  Gu Xuenan (Key Laboratory for Biomechanics and Mechanobiology of Ministry of Education, School of Biological Science and Medical Engineering, Beihang University, Beijing 100191, China) ,  Albert Devon (Laboratory for Biomechanics and Biomaterials, Department of Orthopaedic Surgery, Hannover Medical School, Anna-von-Borries-Strasse 1-7, 30625 Hannover, Germany) ,  Albert Devon (CrossBIT, Center for Biocompatibility and Implant-Immunology, Department of Orthopaedic Surgery, Hannover Medical School, Feodor-Lynen-Strasse 31, 30625 Hannover, Germany) ,  Albert Devon (Swanson School of Engineering, Department of Bioengineering, University of Pittsburgh, Pittsburgh, PA, USA) ,  Kalla Katharina (Laboratory for Biomechanics and Biomaterials, Department of Orthopaedic Surgery, Hannover Medical School, Anna-von-Borries-Strasse 1-7, 30625 Hannover, Germany) ,  Kalla Katharina (CrossBIT, Center for Biocompatibility and Implant-Immunology, Department of Orthopaedic Surgery, Hannover Medical School, Feodor-Lynen-Strasse 31, 30625 Hannover, Germany) ,  Bobe Katharina (Laboratory for Biomechanics and Biomaterials, Department of Orthopaedic Surgery, Hannover Medical School, Anna-von-Borries-Strasse 1-7, 30625 Hannover, Germany) ,  Bobe Katharina (CrossBIT, Center for Biocompatibility and Implant-Immunology, Department of Orthopaedic Surgery, Hannover Medical School, Feodor-Lynen-Strasse 31, 30625 Hannover, Germany) ,  Brauneis Maria (Laboratory for Biomechanics and Biomaterials, Department of Orthopaedic Surgery, Hannover Medical School, Anna-von-Borries-Strasse 1-7, 30625 Hannover, Germany) ,  Brauneis Maria (CrossBIT, Center for Biocompatibility and Implant-Immunology, Department of Orthopaedic Surgery, Hannover Medical School, Feodor-Lynen-Strasse 31, 30625 Hannover, Germany) ,  Janning Carla (Laboratory for Biomechanics and Biomaterials, Department of Orthopaedic Surgery, Hannover Medical School, Anna-von-Borries-Strasse 1-7, 30625 Hannover, Germany) ,  Janning Carla (CrossBIT, Center for Biocompatibility and Implant-Immunology, Department of Orthopaedic Surgery, Hannover Medical School, Feodor-Lynen-Strasse 31, 30625 Hannover, Germany) ,  Nellesen Jens (Institute of Materials Engineering, Technische Universitaet Dortmund, Leonhard-Euler-Strasse 2, 44227 Dortmund, Germany) ,  Czayka Wolfgang (Institute of Materials Engineering, Technische Universitaet Dortmund, Leonhard-Euler-Strasse 2, 44227 Dortmund, Germany) ,  Tillmann Wolfgang (Institute of Materials Engineering, Technische Universitaet Dortmund, Leonhard-Euler-Strasse 2, 44227 Dortmund, Germany) ,  Zheng Yufeng (Department of Materials Science and Engineering, College of Engineering, Peking University, No. 5 Yi-He-Yuan Road, Hai-Dian District, Beijing 100871, China) ,  Witte Frank (Laboratory for Biomechanics and Biomaterials, Department of Orthopaedic Surgery, Hannover Medical School, Anna-von-Borries-Strasse 1-7, 30625 Hannover, Germany) ,  Witte Frank (CrossBIT, Center for Biocompatibility and Implant-Immunology, Department of Orthopaedic Surgery, Hannover Medical School, Feodor-Lynen-Strasse 31, 30625 Hannover, Germany)
資料名： Acta Biomaterialia  (Acta Biomaterialia)
巻： 11  ページ： 554-562  発行年： 2015年 
JST資料番号： W3136A  ISSN： 1742-7061  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 希土類元素は,生物医学応用における生分解性デバイスとして使われるマグネシウム合金のための有望な合金元素候補である。希土類元素は合金のクリープ抵抗と同様に高温強度に著しい影響を及ぼし,それらはマグネシウム耐食性を改善する。ランタン,ネオジムおよびセリウムに焦点を当て,一般的に用いられる希土類元素濃度を有するマグネシウム合金を作製した。低濃度の希土類元素は,インプラント周囲で750μmの幅広い領域内で骨成長を促進しないことを示した。しかし,分解合金からより大きな距離で骨成長の増加が観察された。臨床的および組織学的に,合金およびそれらの腐食生成物は,系統的または局所的細胞毒性効果を引き起こさなかった。ミクロトモグラフィとin vitro実験を用いて,マグネシウム-希土類元素合金がin vitroとin vivoの両方で低い腐食速度を示した。ランタンおよびセリウム含有合金は同等の速度で分解したが,ネオジム含有合金は最低の腐食速度を示した。Copyright 2021 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 合金 ,  *セリウム ,  *ネオジム ,  *マグネシウム ,  *ランタン ,  マグネシウム合金 ,  耐食性 ,  腐食速度 ,  合金元素 ,  *希土類元素 ,  ネオジム含有合金 ,  微生物分解性 ,  細胞毒性 ,  *生体適合性 ,  in vitro実験

著者キーワード (5件)： マグネシウム合金 ,  希土類元素 ,  生体適合性 ,  生分解性インプラント ,  in vitro

分類 (2件)： 医用素材  (GA05040H) ,  腐食  (WB03030B)

タイトルに関連する用語 (7件)： マグネシウム ,  生物分解 ,  生体適合性 ,  希土類元素 ,  ランタン ,  ネオジム ,  セリウム