レーザ材料と温度センシングのためのネオジムドープゲルマノテルライトガラス【JST・京大機械翻訳】

Neodymium-doped germanotellurite glasses for laser materials and temperature sensing

著者 (5件)： Lukaszewicz M. (Institute of Low Temperature and Structure Research, Polish Academy of Sciences, Okolna 2, 50-422, Wroclaw, Poland) ,  Klimesz B. (Opole University of Technology, Proszkowska 76, 45-758, Opole, Poland) ,  Szmalenberg A. (School of Electrical and Data Engineering, Faculty of Engineering and IT, University of Technology Sydney, 15 Broadway, Ultimo, NSW, 2007, Australia) ,  Ptak M. (Institute of Low Temperature and Structure Research, Polish Academy of Sciences, Okolna 2, 50-422, Wroclaw, Poland) ,  Lisiecki R. (Institute of Low Temperature and Structure Research, Polish Academy of Sciences, Okolna 2, 50-422, Wroclaw, Poland)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 860  ページ： Null  発行年： 2021年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 溶融急冷法を用いて,種々の(0.2~3%)Nd濃度のGTSN:Nd(GeO_2-TeO_2-SrF_2-Nb_2O_5-Nd_2O_3)ガラスを得た。それらの熱特性を示差走査熱量測定を用いて評価し,非常に好ましいガラス熱安定性を示した。ガラス構造をXRD,IRおよびRaman分光法を用いて分析した。ゲルマニウム酸塩,テルライトおよびフッ化物光学系の利点を組み合わせて,吸収,発光および蛍光寿命分光法のような光学分光法で証明されたように,有望なガラスレーザ材料を達成した。Nd励起準位からの発光バンド間の蛍光強度比を利用して,ルミネセンス温度測定のいくつかのモデルをGTSN:Ndに対して確立した。モデルの1つをレーザパワー依存性実験で試験し,高出力光励起時の温度上昇の推定を可能にした。非接触温度測定用のビルトイン法と共に,材料の大きな熱安定性と分光性能は,GTSN:Ndをガラスベース光学活性素子のための有望な材料にする。Copyright 2021 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  温度測定 ,  *ガラス ,  発光 ,  光ポンピング ,  ルミネセンス ,  *レーザ材料 ,  *ネオジム ,  フッ化物 ,  *ドーピング ,  急冷 ,  示差走査熱量測定 ,  蛍光寿命
準シソーラス用語： 蛍光強度 ,  *テルライトガラス , 【Automatic Indexing@JST】

著者キーワード (5件)： ゲルマニウム酸塩ガラス ,  テルライトガラス ,  ネオジム ,  ルミネセンス温度測定 ,  光学分光法

分類 (1件)： 固体レーザ  (BD04080W)

タイトルに関連する用語 (2件)： レーザ材料 ,  温度センシング