グルコース検出感度増強のためのCuOの制御可能な表面酸素空孔の顕著な影響【JST・京大機械翻訳】

Significant influence of controllable surface oxygen vacancies of CuO for enhancing sensitivity of glucose detection

著者 (21件)： Wang Shengbao (Institute of Advanced Electrochemical Energy, School of Materials Science and Engineering, Xi’an University of Technology, Xi’an 730048, China) ,  Wang Shengbao (Shaanxi International Joint Research Centre of Surface Technology for Energy Storage Materials, Xi’an 730048, China) ,  Yang Huijuan (Institute of Advanced Electrochemical Energy, School of Materials Science and Engineering, Xi’an University of Technology, Xi’an 730048, China) ,  Yang Huijuan (Shaanxi International Joint Research Centre of Surface Technology for Energy Storage Materials, Xi’an 730048, China) ,  Yi Xiaoyu (Institute of Advanced Electrochemical Energy, School of Materials Science and Engineering, Xi’an University of Technology, Xi’an 730048, China) ,  Yi Xiaoyu (Shaanxi International Joint Research Centre of Surface Technology for Energy Storage Materials, Xi’an 730048, China) ,  Maleki Kheimeh Sari Hirbod (Institute of Advanced Electrochemical Energy, School of Materials Science and Engineering, Xi’an University of Technology, Xi’an 730048, China) ,  Maleki Kheimeh Sari Hirbod (Shaanxi International Joint Research Centre of Surface Technology for Energy Storage Materials, Xi’an 730048, China) ,  Zhang Xuan (Department of Materials Engineering, KU Leuven, 3001 Leuven, Belgium) ,  Wang Tao (State Key Laboratory of Physical Chemistry of Solid Surfaces, Innovation Center of Chemistry for Energy Materials, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005, China) ,  Zhou Zhiyou (State Key Laboratory of Physical Chemistry of Solid Surfaces, Innovation Center of Chemistry for Energy Materials, College of Chemistry and Chemical Engineering, Xiamen University, Xiamen 361005, China) ,  Cao Bin (Institute of Advanced Electrochemical Energy, School of Materials Science and Engineering, Xi’an University of Technology, Xi’an 730048, China) ,  Cao Bin (Shaanxi International Joint Research Centre of Surface Technology for Energy Storage Materials, Xi’an 730048, China) ,  Qin Jian (Institute of Advanced Electrochemical Energy, School of Materials Science and Engineering, Xi’an University of Technology, Xi’an 730048, China) ,  Qin Jian (Shaanxi International Joint Research Centre of Surface Technology for Energy Storage Materials, Xi’an 730048, China) ,  Wang Jingjing (Institute of Advanced Electrochemical Energy, School of Materials Science and Engineering, Xi’an University of Technology, Xi’an 730048, China) ,  Wang Jingjing (Shaanxi International Joint Research Centre of Surface Technology for Energy Storage Materials, Xi’an 730048, China) ,  Li Wenbin (Institute of Advanced Electrochemical Energy, School of Materials Science and Engineering, Xi’an University of Technology, Xi’an 730048, China) ,  Li Wenbin (Shaanxi International Joint Research Centre of Surface Technology for Energy Storage Materials, Xi’an 730048, China) ,  Li Xifei (Institute of Advanced Electrochemical Energy, School of Materials Science and Engineering, Xi’an University of Technology, Xi’an 730048, China) ,  Li Xifei (Shaanxi International Joint Research Centre of Surface Technology for Energy Storage Materials, Xi’an 730048, China)
資料名： Applied Surface Science  (Applied Surface Science)
巻： 574  ページ： Null  発行年： 2022年 
JST資料番号： B0707B  ISSN： 0169-4332  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 欠陥工学の1つとしての酸素空孔の構築は,電極触媒活性を高める有望な戦略である。ここでは,酸素空孔を富化したCuOナノフレークを,撹拌による簡単なワンポット法により成功裏に合成した。高角度環状暗視野走査,X線光電子分光法および電子スピン共鳴分光法を,豊富な酸素空孔の存在を確認するために実施した。合成したままのCuOナノフレークは酸素空孔で濃縮され,+0.22Vの低い開始電位,4870μAmM-1cm-2の超高感度,及び0.5μMの低い検出限界でグルコース検出に優れた性能を示した。CuOナノフレークの優れた性能は表面酸素空孔に起因し,吸着ヒドロキシルイオンを加速し,Cu3+化学種の生成を促進し,それによって1電位を減少させ,グルコース酸化を促進した。本研究は,酸素空孔を構築することによるグルコース検出のための他の効率的な触媒の合理的な設計指針として役立つであろう。Copyright 2021 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 吸着 ,  電位 ,  検出限界 ,  水酸化物イオン ,  高感度 ,  X線光電子分光法 ,  化学種 ,  *酸化第二銅 ,  ヘキソース ,  アルドース
準シソーラス用語： 検出能 ,  環状 ,  *酸素空格子点 ,  ナノフレーク ,  電極触媒活性 ,  グルコース酸化 , 【Automatic Indexing@JST】

著者キーワード (4件)： CuO ,  酸素空孔 ,  グルコース酸化 ,  超高感度

分類 (2件)： その他の触媒  (CB06123Z) ,  不均一系触媒反応  (CB06100E)

物質索引 (1件)： グルコース

タイトルに関連する用語 (5件)： グルコース ,  検出感度 ,  増強 ,  CuO ,  酸素空孔