Cr(VI)光還元のための鋼スラグ上のナノ構造マグネシウムフェライトのその場構築【JST・京大機械翻訳】

In-situ constructing nanostructured magnesium ferrite on steel slag for Cr(VI) photoreduction

著者 (13件)： Sun Lingmin (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  Wu Junshu (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  Wang Jinshu (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  Yang Yilong (Henan Key Laboratory of Water Pollution Control and Rehabilitation Technology, Henan University of Urban Construction, Pingdingshan 467036, China) ,  Xu Meng (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  Liu Jingchao (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  Yang Chen (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  Cai Yongfeng (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  He Heng (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  Du Yucheng (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  Hu Peng (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  Li Yongli (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China) ,  Li Hongyi (Key Laboratory of Advanced Functional Materials, Ministry of Education, Faculty of Materials and Manufacturing, Beijing University of Technology, Beijing 100022, China)
資料名： Journal of Hazardous Materials  (Journal of Hazardous Materials)
巻： 422  ページ： Null  発行年： 2022年 
JST資料番号： B0362A  ISSN： 0304-3894  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 鋼スラグ表面に鉄リッチRO相(MgO_0.239FeO_0.761)をナノ構造Mg_0.04Fe_2.96O_4層に変換する革新的方法を作成した。相変化過程を調べ,サリチル酸修飾とアルカリ焙焼手順が比表面積を0.46m2/g(生鋼スラグ)から69.5m2/g(Mg_0.04Fe_2.96O_4)に顕著に増大させ,Mg_0.04Fe_2.96O_4の生成が,生鋼スラグよりも2倍増加で可視光とCr(VI)変換の吸収を高めることが分かった。Mg_0.04Fe_2.96O_4上のH_2C_2O_4配位子とFe金属部分の間の表面錯化は,配位子対金属電荷移動機構に基づく可視光照射下での分子内電子移動を誘起し,従ってCr(VI)光還元をもたらし,触媒効率は固有のpH=5.5条件下でCr(VI)(40mg/L)に対して90%以上であった。さらに,磁気分離に基づくリサイクル性試験は,光反応性がMg_0.04Fe_2.96O_4層のMg含有量に密接に関連し,Mg浸出が起こり,最終的に立方晶スピネル構造Fe_3O_4を生成することを示した。本研究は,表面反応性と適用電位が化学暴露履歴と表面変換によって大きく変化できる製鋼スラグのポスト使用段階における表面官能化の重要性を強調する。また,それはマグネシウムフェライト光触媒の準安定状態機構を研究するための貴重な参照を提供する。Copyright 2021 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 相転移 ,  鉄 ,  *マグネシウム ,  焙焼 ,  *光還元 ,  錯体生成 ,  可視光 ,  立方晶系 ,  準安定状態 ,  *六価クロム ,  光触媒 ,  *製鋼スラグ ,  *ナノ構造 ,  芳香族カルボン酸 ,  フェノール類 ,  ヒドロキシ酸
準シソーラス用語： 可視光照射 , 【Automatic Indexing@JST】

著者キーワード (3件)： 製鋼スラグ ,  マグネシウムフェライト ,  Cr(VI)還元

分類 (2件)： 産業廃水処理  (SC03080D) ,  重金属とその化合物一般  (SB05021R)

物質索引 (1件)： サリチル酸

タイトルに関連する用語 (6件)： Cr ,  光還元 ,  鋼スラグ ,  ナノ構造 ,  マグネシウムフェライト ,  構築