高温に曝されたハイブリッドフライアッシュ/スラグベースジオポリマの劣化機構【JST・京大機械翻訳】

Degradation mechanism of hybrid fly ash/slag based geopolymers exposed to elevated temperatures

著者 (6件)： Luo Y. (Department of the Built Environment, Eindhoven University of Technology, P.O. Box 513, 5600MB Eindhoven, the Netherlands) ,  Li S.H. (Department of the Built Environment, Eindhoven University of Technology, P.O. Box 513, 5600MB Eindhoven, the Netherlands) ,  Klima K.M. (Department of the Built Environment, Eindhoven University of Technology, P.O. Box 513, 5600MB Eindhoven, the Netherlands) ,  Brouwers H.J.H. (Department of the Built Environment, Eindhoven University of Technology, P.O. Box 513, 5600MB Eindhoven, the Netherlands) ,  Yu Qingliang (Department of the Built Environment, Eindhoven University of Technology, P.O. Box 513, 5600MB Eindhoven, the Netherlands) ,  Yu Qingliang (School of Civil Engineering, Wuhan University, 430072 Wuhan, PR China)
資料名： Cement and Concrete Research  (Cement and Concrete Research)
巻： 151  ページ： Null  発行年： 2022年 
JST資料番号： E0724A  ISSN： 0008-8846  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 高温適用のためのアルカリ活性化フライアッシュ(AAF)の有望な代替として,高温下のアルカリ活性化フライアッシュ/GGBS(AAFS)の分解機構は明らかではない。本研究では,800°CまでのAAFSの物理化学的特性を調べ,熱挙動に対する相乗効果を示した。亀裂の定量的評価を開発し,亀裂挙動を学習した。結果は,亀裂密度が超音波パルス速度と線形関係を示すことを明らかにした。亀裂密度と圧縮強度は100°C前に正の相関を示したが,100°C以上では負の関係を示した。ジオポリマーへのスラグの添加は,更なるジオポリマー化や粘性焼結のようなジオポリマー挙動に,さらに,コンパクトな構造と不安定なハイブリッドゲルによる熱損傷を悪化させる。AAFとAAFSの概念モデルを,高温下の低スラグ含有ジオポリマーの分解機構を説明するために提案した。Copyright 2021 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 亀裂 ,  *高温 ,  焼結 ,  粘性 ,  *スラグ ,  *フライアッシュ ,  相乗作用 ,  線形性 ,  圧縮強さ ,  超音波パルス
準シソーラス用語： 物理化学的性質 ,  *ジオポリマ ,  劣化機構 ,  熱挙動 ,  ハイブリッドゲル , 【Automatic Indexing@JST】

著者キーワード (5件)： アルカリ活性化 ,  ハイブリッドバインダ ,  高温 ,  微小亀裂特性 ,  機械的進化

分類 (1件)： セメントの性質・分析  (YC05040F)

タイトルに関連する用語 (1件)： フライアッシュ