サトウキビバガスに由来する活性炭の超高表面積【JST・京大機械翻訳】

Extremely high surface area of activated carbon originated from sugarcane bagasse

著者 (6件)： Dwiyaniti Murie (Department of Electrical Engineering Faculty of Engineering, Universitas Indonesia, Depok 16424, Indonesia) ,  Elang Barruna A.G (Department of Electrical Engineering Faculty of Engineering, Universitas Indonesia, Depok 16424, Indonesia) ,  Muhamad Naufal R (Department of Electrical Engineering Faculty of Engineering, Universitas Indonesia, Depok 16424, Indonesia) ,  Subiyanto Iyan (Department of Electrical Engineering Faculty of Engineering, Universitas Indonesia, Depok 16424, Indonesia) ,  Setiabudy Rudy (Department of Electrical Engineering Faculty of Engineering, Universitas Indonesia, Depok 16424, Indonesia) ,  Hudaya Chairul (Department of Electrical Engineering Faculty of Engineering, Universitas Indonesia, Depok 16424, Indonesia)
資料名： IOP Conference Series: Materials Science and Engineering  (IOP Conference Series: Materials Science and Engineering)
巻： 909  号： 1  ページ： 012018 (8pp)  発行年： 2020年 
JST資料番号： W5559A  ISSN： 1757-8981  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 本研究では,サトウキビバガス由来の活性炭の非常に高い比表面積を乾燥化学活性化により生産した。このプロセスでは,KOHを化学試薬として用い,KOH粉末と直接混合サトウキビバガス炭素を固体の形で処理した。特に,含浸比と活性化温度の影響を調べた。調製したままの活性炭をBrunauer-Emmett-Teller(BET)によって特性化し,それは活性炭の表面積とRamanスペクトル分析を決定し,材料特性の振動モードを調べた。活性炭の最大比表面積は800°Cで3554m2/gに達し,含浸率は1:4であった。さらに,活性炭のRamanスペクトルは,GおよびG-1バンドを持つため,含浸比1:2および1:3のサンプルに対してグラファイト構造を示した。この材料は電池を作るのに不可欠である。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： Ramanスペクトル ,  電池 ,  表面積 ,  粉体 ,  含浸 ,  *活性炭 ,  比表面積 ,  振動モード ,  キャラクタリゼーション ,  Raman分光分析
準シソーラス用語： 材料特性 ,  *サトウキビバガス , 【Automatic Indexing@JST】

分類 (1件)： 炭素とその化合物  (YB02060D)

タイトルに関連する用語 (3件)： サトウキビバガス ,  活性炭 ,  表面積