高窒素オーステナイト系ステンレス鋼ボイラタンク溶接部の破壊解析【JST・京大機械翻訳】

Failure Analysis of the High Nitrogen Austenitic Stainless-Steel Boiler Tank Weldments

著者 (4件)： Vijayan Vijeesh (Department of Mechanical Engineering, NMAMIT (An autonomous college under Visvesvariah Technological University), Nitte, Karkala, Udupi, India) ,  Ravichandran G. (Department of Mechanical Engineering, NMAMIT (An autonomous college under Visvesvariah Technological University), Nitte, Karkala, Udupi, India) ,  Rao Muralidhara (Department of Mechanical Engineering, NMAMIT (An autonomous college under Visvesvariah Technological University), Nitte, Karkala, Udupi, India) ,  Karinka Shashikantha (Department of Mechanical Engineering, NMAMIT (An autonomous college under Visvesvariah Technological University), Nitte, Karkala, Udupi, India)
資料名： Journal of Failure Analysis and Prevention  (Journal of Failure Analysis and Prevention)
巻： 21  号： 3  ページ： 976-982  発行年： 2021年 
JST資料番号： W4576A  ISSN： 1547-7029  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： ドイツ (DEU)  言語： 英語 (EN)

抄録/ポイント： 本論文では,米の煮沸と籾殻の工場に加工された熱水を貯蔵するために使用されるステンレス鋼(SS)タンクの亀裂と漏れの理由を調べた。ラジオグラフィー,光学金属組織学,走査電子顕微鏡,EDAXを用いたタンク試料の詳細な分析は,応力腐食割れ(SCC)が破壊の主な理由であることを明らかにした。好ましい微細構造,環境および応力の存在は,タンク溶接部におけるSCCの核形成および伝播を促進した。選択したステンレスグレードにおける微細構造の進展を研究し,Scheffler-Delongダイヤグラムを用いて議論した。低ニッケル,高窒素オーステナイト系ステンレス鋼におけるマルテンサイトの形成が,機械的性質に大きく影響し,SCCを促進することが観察された。SS316合金と比較して材料の孔食抵抗の減少は,SCCの核形成サイトとして作用するピットの開始における重要因子であった。Copyright ASM International 2021 Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： 核形成 ,  機械的性質 ,  合金 ,  走査電子顕微鏡 ,  *窒素 ,  ニッケル ,  *ステンレス鋼 ,  応力腐食割れ ,  *溶接部 ,  マルテンサイト ,  *貯槽 ,  ラジオグラフィー ,  *オーステナイト系ステンレス鋼 ,  耐孔食性
準シソーラス用語： *破壊解析 , 【Automatic Indexing@JST】

著者キーワード (4件)： 応力腐食割れ ,  孔食 ,  200シリーズステンレス鋼 ,  マルテンサイト

分類 (2件)： 腐食  (WB03030B) ,  溶接部  (WC07100I)

タイトルに関連する用語 (6件)： 窒素 ,  オーステナイト系ステンレス鋼 ,  ボイラ ,  タンク ,  溶接部 ,  破壊解析