粉末冶金で作製したFeCrNi中エントロピー合金の腐食挙動と機構【JST・京大機械翻訳】

Corrosion behavior and mechanism of FeCrNi medium entropy alloy prepared by powder metallurgy

著者 (6件)： Zhou Zhengyan (State Key Lab of Powder Metallurgy, Central South University, Changsha 410083, PR China) ,  Liu Bin (State Key Lab of Powder Metallurgy, Central South University, Changsha 410083, PR China) ,  Guo Wenmin (State Key Lab of Powder Metallurgy, Central South University, Changsha 410083, PR China) ,  Fu Ao (State Key Lab of Powder Metallurgy, Central South University, Changsha 410083, PR China) ,  Duan Heng (State Key Lab of Powder Metallurgy, Central South University, Changsha 410083, PR China) ,  Li Weihua (State Key Lab of Powder Metallurgy, Central South University, Changsha 410083, PR China)
資料名： Journal of Alloys and Compounds  (Journal of Alloys and Compounds)
巻： 867  ページ： Null  発行年： 2021年 
JST資料番号： D0083A  ISSN： 0925-8388  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： オランダ (NLD)  言語： 英語 (EN)

抄録/ポイント： 本研究では,3.5wt%NaCl溶液中で粉末冶金法により調製した新しいFeCrNi媒体エントロピー合金(MEA)の腐食挙動と機構を研究した。その結果,316L SSと比較して,FeCrNi MEAは,より正の破壊電位(0.928V_SCE)およびより低い電流密度(8.317×10-8A/cm2)を有する優れた耐食性を示した。FeCrNi MEAの表面に形成した不動態膜はCrリッチで欠陥の少ない膜である。同時に,それは強い自己修復能力を有した。均一な微細構造と高いCr含有量は良好な耐食性能の原因である。Copyright 2021 Elsevier B.V., Amsterdam. All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： *エントロピー ,  *合金 ,  電位 ,  微細構造 ,  耐食性 ,  不動態皮膜 ,  *粉末冶金 ,  塩化ナトリウム ,  媒質 ,  電流密度
準シソーラス用語： 自己修復 ,  SUS316L ,  *腐食挙動 , 【Automatic Indexing@JST】

著者キーワード (4件)： 中エントロピー合金 ,  耐食性 ,  受動フィルム ,  粉末冶金

分類 (2件)： 腐食  (WB03030B) ,  圧粉,焼結  (WC02030X)

タイトルに関連する用語 (5件)： 粉末冶金 ,  作製 ,  エントロピー ,  合金 ,  腐食挙動