Eu3+,Lu3+共ドープCa_0.3Sr_0.7Mo_1-xW_xO_4赤色発光蛍光体のゾル-ゲル合成とルミネセンス性能【JST・京大機械翻訳】

Sol-gel synthesis and luminescent performance of Eu³⁺, Lu³⁺ co-doped Ca_0.3Sr_0.7Mo_1-xW_xO₄ red-emitting phosphor

著者 (5件)： Xie Huidong (School of Chemistry and Chemical Engineering, Xi’an University of Architecture and Technology, Xi’an, China) ,  Chen Cheng (School of Chemistry and Chemical Engineering, Xi’an University of Architecture and Technology, Xi’an, China) ,  Li Jie (School of Chemistry and Chemical Engineering, Xi’an University of Architecture and Technology, Xi’an, China) ,  He Yingying (School of Chemistry and Chemical Engineering, Xi’an University of Architecture and Technology, Xi’an, China) ,  Wang Na (College of Architecture and Civil Engineering, Xi’an University of Science and Technology, Xi’an, China)
資料名： Inorganic and Nano-Metal Chemistry  (Inorganic and Nano-Metal Chemistry)
巻： 51  号： 10  ページ： 1297-1305  発行年： 2020年 
JST資料番号： W5880A  ISSN： 2470-1556  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： イギリス (GBR)  言語： 英語 (EN)

抄録/ポイント： 赤色発光Ca_0.3Sr_0.7-1.5y-1.5zMo_1-xW_xO_4:Eu_yLu_z(x=0-1,y,z=0~0.14)蛍光体をゾル-ゲル法により合成した。ルミネセンス特性に及ぼす焼成温度,Lu3+およびEu3+濃度,およびW/Mo比の影響を詳細に研究した。蛍光体をXRD,SEMおよびXPSによって特性化した。ルミネセンス特性を蛍光スペクトルで測定した。実験はLu3+とEu3+共ドープ蛍光体が619nmに強い赤色発光を持つことを示した。x=0.2,y=0.1およびz=0.1において,900°Cで焼成した蛍光体は最大発光強度を示した。蛍光体の温度依存発光強度は,調製したままの蛍光体の発光強度が熱的に安定であることを示した。減衰の結果から,MoO_42-からEu3+へのエネルギー移動効率は,Mo6+濃度の増加に伴い0から0.2に増加した。Please refer to the publisher for the copyright holders. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  エネルギー移動 ,  蛍光スペクトル ,  *蛍光体 ,  *ルミネセンス ,  *モリブデン ,  *ゲル ,  温度依存性 ,  *ドーピング ,  灰重石 ,  *ゾル-ゲル法
準シソーラス用語： 発光強度 ,  焼成温度 ,  *赤色発光 ,  赤色蛍光体 , 【Automatic Indexing@JST】

著者キーワード (4件)： 灰重石 ,  ゾル-ゲル合成 ,  LED ,  ルミネセンス

分類 (1件)： 無機化合物のルミネセンス  (BM08093J)

タイトルに関連する用語 (4件)： ドープ ,  赤色発光蛍光体 ,  ゾル-ゲル合成 ,  ルミネセンス