低温NH_3-SCR性能強化のためのMnO_xの負荷によるV_2O_5-WO_3/TiO_2触媒の改質【JST・京大機械翻訳】

Modification of V2O5-WO3/TiO2 Catalyst by Loading of MnOx for Enhanced Low-Temperature NH3-SCR Performance

著者 (7件)： Zhang Xianlong (School of Chemistry and Chemical Engineering, Hefei University of Technology, Hefei 230009, China) ,  Zhang Xianlong (Anhui Province Key Laboratory of Advanced Catalytic Materials and Reaction Engineering, Hefei University of Technology, Hefei 230009, China) ,  Diao Qinchao (School of Chemistry and Chemical Engineering, Hefei University of Technology, Hefei 230009, China) ,  Hu Xiaorui (School of Chemistry and Chemical Engineering, Hefei University of Technology, Hefei 230009, China) ,  Wu Xueping (School of Chemistry and Chemical Engineering, Hefei University of Technology, Hefei 230009, China) ,  Xiao Kesong (Instrumental Analysis Center, Hefei University of Technology, Hefei 230009, China) ,  Wang Junwei (College of Chemistry and Chemical Engineering, Anqing Normal University, Anqing 246011, China)
資料名： Nanomaterials (Web)  (Nanomaterials (Web))
巻： 10  号： 10  ページ： 1900  発行年： 2020年 
JST資料番号： U7252A  ISSN： 2079-4991  資料種別： 逐次刊行物 (A)
記事区分： 原著論文  発行国： スイス (CHE)  言語： 英語 (EN)

抄録/ポイント： 中温で通常用いられる市販の選択的触媒還元(SCR)触媒としてのV_2O_5-WO_3/TiO_2を,低温でその性能を高める目的で,MnO_xの負荷によって改質した。酸化マンガンを,含浸(I),沈殿(P),およびその場成長(S)の方法によって,V-W/Tiモノリスに負荷した。各修飾触媒のSCR活性を100340Cの範囲で調べた。触媒を,比表面積と細孔径決定(BET),X線回折(XRD),温度プログラム還元(TPR)などによって特性評価した。結果は,MnO_xの負荷が280Cより低い温度でSCR活性を著しく強化することを示した。その場成長法で調製した触媒はSCRに対して最も活性であることが分かった。Copyright 2021 The Author(s) All rights reserved. Translated from English into Japanese by JST.【JST・京大機械翻訳】

シソーラス用語： X線回折 ,  *低温 ,  含浸 ,  沈殿 ,  比表面積 ,  酸化マンガン ,  中温 ,  細孔径 ,  キャラクタリゼーション ,  TPR【触媒】
準シソーラス用語： SCR【触媒】 ,  モノリス ,  酸化マンガン(II) , 【Automatic Indexing@JST】

著者キーワード (5件)： NH_3-SCR ,  V-W/Ti ,  低温 ,  酸化マンガン ,  その場成長

分類 (2件)： 有害ガス処理法  (SC04030H) ,  その他の触媒  (CB06123Z)

引用文献 (32件)：

• Xu, W.J.; Zhang, G.X.; Chen, H.W.; Zhang, G.M.; Han, Y.; Chang, Y.C.; Gong, P. Mn/beta and Mn/ZSM-5 for the low-temperature selective catalytic reduction of NO with ammonia: Effect of manganese precursors. Chin. J. Catal. 2018, 39, 118-127.
• Park, E.; Chin, S.; Jeong, J.; Jurng, J. Low-temperature NO oxidation over Mn/TiO2, nanocomposite synthesized by chemical vapor condensation: Effects of Mn precursor on the surface Mn species. Microporous Mesoporous Mater. 2012, 163, 96-101.
• Ji, P.D.; Gao, X.; Du, X.S.; Zheng, C.H.; Luo, Z.Y.; Cen, K.F. Relationship between the molecular structure of V2O5/TiO2 catalysts and the reactivity of SO2 oxidation. Catal. Sci. Technol. 2016, 6, 1187-1194.
• Zhao, X.; Hang, L.; Namuangruk, S.; Hu, H.; Hu, X.N.; Shi, L.Y.; Zhang, D.S. Morphology dependent performance of Zr-CeVO4/TiO2 for selective catalytic reduction of NO with NH3. Catal. Sci. Technol. 2016, 6, 5543-5553.
• Ding, S.P.; Liu, F.D.; Shi, X.Y.; Liu, K.; Lian, Z.H.; Xie, L.J.; He, H. Significant Promotion Effect of Mo Additive on a Novel Ce-Zr Mixed Oxide Catalyst for the Selective Catalytic Reduction of NOx with NH3. ACS Appl. Mater. Interfaces 2015, 7, 9497.

タイトルに関連する用語 (5件)： 低温 ,  SCR ,  強化 ,  触媒 ,  改質